Abstract:Two mesostructured MCM-41 silicas that differ dramatically in hydrothermal stability have been examined by (29)Si MAS NMR spectroscopy and pair distribution function (PDF) analysis of synchrotron X-ray scattering data. The less stable mesostructure assembled from sodium silicate and the substantially more stable derivative made from fumed silica possess equivalent local framework wall structures, as judged by NMR and PDF methods. Approximately 80% of the SiO(4) tetrahedra are fully cross-linked as Q(4) (Si(OSi)(4)) units in both calcined samples. Additionally, the structural correlation distances for the two materials are nearly identical, having values of 1.62(1), approximately 2.60, and 3.09(1) A for the Si-O, O-O, and nearest neighbor Si-Si distances in the framework. Sodium ions in the framework play a crucial role in limiting the hydrothermal stability of the mesostructure. Residual sodium ( approximately 0.05-0.10% Na(2)O) is retained in the MCM-41 made from sodium silicate, even after two ion exchange reactions with ammonium ions in more than 300 - fold excess. The entrapped framework sodium ions catalyze the collapse of the mesopores upon exposure to 20% steam at 800 degrees C for 5 h. The sodium - free mesostructure assembled from fumed silica retains an open framework under the same hydrothermal conditions. The stability of the fumed silica derivative, however, is greatly compromised when doped with as little as 0.10% Na(2)O, thus confirming the deleterious effect of sodium on hydrothermal stability.

Thermal Stability of Structural Aluminum in the Mesoporous Molecular Sieve MCM-41

Effect Of Structural Aluminum On The Mesoporous Structure Of Mcm-41

Preparation of mesoporous Al-MCM-41 with stable tetrahedral aluminum using ionic liquids as a single template

Study on the hydrothermal stability of MCM-41 via secondary restructure

Novel route in the synthesis of MCM-41 containing framework aluminum and its characterization

Synthesis and Characterization of AlMCM-41 Molecular Sieves

Role of framework sodium versus local framework structure in determining the hydrothermal stability of MCM-41 mesostructures

Investigation of the Microporous Structure and Non-Framework Aluminum Distribution in Dealuminated Nanosized HZSM-5 Zeolite by 129xe NMR Spectroscopy

Comparison of disordered mesoporous aluminosilicates with highly ordered Al-MCM-41 on stability, acidity and catalytic activity

Structural Characteristics Of Mcm-41 Synthesized In-Situ On Silica

IR Spectroscopic Studies of the Acidic Properties of the Mesoporous Molecular Sieve MCM-41

Surface Properties of Al-Functionalized Mesoporous MCM-41 and the Melting Behavior of Water in Al-MCM-41 Nanopores

Preparation of MCM-41 with high thermal stability and complementary textural porosity

Effect of Aluminum on the Formation of Zeolite MCM-22 and Kenyaite

New Mineralization Agents for the Synthesis of MCM-41

Temperature-Driven Structural Evolution during Preparation of MCM-41 Mesoporous Silica

STUDY ON ACID PROPERTIES OF MCM-41 MESOPOROUS MOLECULAR SIEVE MATERIALS

Influence of cations (Li+, Na+, K+)for synthesis mesoporous molecular sieve MCM-41 and their properties

Synthesis of Mesoporous Molecular Sieve Al-MCM-41 in Ammonia Water and Its Characterization

Stable Tetrahedral Aluminum Sites in Hexagonal Mesoporous Aluminosilicates

Synthesis of Aluminosilicate MCM-41 Using Oligomeric Surfactant As Template