Fabrication and Performance Test of Solid Oxide Fuel Cells with Screen-Printed Yttria-Stabilized Zirconia Electrolyte Membranes
Yaohui Zhang,Zhe Lü,Xiqiang Huang,Maozhong An,Bo Wei,Wenhui Su
DOI: https://doi.org/10.1007/s10008-010-1257-8
IF: 2.747
2010-01-01
Journal of Solid State Electrochemistry
Abstract:Yttria-stabilized zirconia (YSZ) membranes were deposited onto porous NiO–YSZ anode supports by screen printing. Combined with La0.7Sr0.3MnO3–YSZ composite cathode, the prepared anode-supported solid oxide fuel cells (SOFCs) were electrochemically tested. A typical SOFC with a 30-μm-thick YSZ electrolyte membrane gave the maximum power densities (MPDs) of 0.26, 0.53, 0.78, and 1.03 W/cm2 at 650, 700, 800, and 850 °C, respectively, using hydrogen as fuel and stationary air as oxidant. Replacement of stationary air with pure oxygen flow exerted a significant positive effect on the MPDs of the cell. Using 100- and 200-ml/min oxygen as oxidants, the MPDs of the cell were enhanced 35.3% and 68.6%, respectively. Polarization analysis indicated that, at the MPD points, the electrode polarization resistances accounted for 80% of the cell total resistances.