Abstract:The solidification behaviours and microstructural characteristics of both ZA27/SiCp composites and monolithic ZA27 alloy were studied by using differential scanning calorimetry, scanning electron microscopy, transmission electron microscopy, electron probe microanalysis, and X-ray diffraction, It was found that there were differences in the transformation temperature and volume fraction of the phases, although the solidification process was almost identical for the composite and the monolithic alloy. The incorporation of SiC particles in the ZA27 alloy led to slight refinement of primary grains and reduced volume fraction of eutectic-like phase. The SiC particles obstructed Zn diffusion in the residual melt during the formation of proeutectic beta phase, but promoted Zn diffusion from alpha (Al) to eta (Zn) phase during eutectoid transformation. During solidification, Cu was mainly segregated in the final solidification regions; Mg was present not only in the matrix but also on SiC particles; and oxide inclusions were mainly distributed around SiC particles, The matrix microstructure for both materials mainly consisted of primary cores of Al rich alpha + eta eutectoid; beta' phase resulting from the eutectoid transformation of the proeutectic beta phase; and Zn rich alpha + eta eutectoid resulting from the eutectoid transformation of the eutectic-like phase. The SiC particles were mainly distributed around the primary grains, Several new phases based on the Al-Zn-Mg-Cu system and interfacial reaction products, including Al21Fe3Si, Cu5Zn8, Mg6Cu3Al7, MgAl2O4, and amorphous oxide inclusions, were identified in the final solidification regions. The nucleation of both primary alpha phase and eutectic-like alpha + eta phase at the surface of SIC particles and their crystallographic orientation relationships were investigated theoretically and experimentally. No distinct crystallographic orientation relationship between the matrix and SiC has been identified, although the mismatch between (0001)(SiC) and (111)(alpha) was calculated to be as small as 7.6%.

450 Degrees C Isothermal Section Of The Zn-Fe-Co-Si Quaternary System At The Zinc-Rich Corner

Experimental study of the phase relations in the Fe–Cr–Si ternary system at 700°C

Experimental Study on Phase Relationships in the Co-rich Portion of the Co–Ti–Zr System

Phase equilibria of the Co-Ni-Zr system at 1198 K

Isothermal Section Of Mn-Zr-Si Ternary System At 600 Degrees C

Microstructure and phase components of the as-cast Cu-0.4%Cr-0.12%Zr-0.01%Si

Isothermal Section of Ternary Sn-Zn-Ni Phase Equilibria at 250 °C

Chemical Reactions in the Co–Si–C System

Experimental Investigation of Phase Equilibria in the Co-Ta-Si Ternary System

Phase equilibria in the Fe-Ti-Zr system at 1023 K

Phase Equilibria in the Ni-Sn-Zn System at 500°C

The Co–Ni–Zr Phase Diagram in the Zr–ZrCo–ZrNi Region I. Phase Equilibria in the Zr–ZrCo–ZrNi System at Subsolidus Temperature, 900°C, and 800°C

Characterisation of Fe Distribution in the Liquid–Solid Boundary of Al–Zn–Mg–Si Alloy Using Synchrotron X-ray Fluorescence Microscopy

Experimental determination of isothermal sections for the Co-rich corner of the Co-Cr-Ti system at 800 and 900 °C

The melting diagram of the Ti-corner of the Ti–Zr–Si system and mechanical properties of as-cast compositions

Phase Equilibria of the Sn-Ag-Cu-Ni Quaternary System at the Sn-Rich Corner

Structure and phase transformation for Co72.7C 11.8Si15.5 magnetic alloy quenched at high temperature

Phase Equilibria In The Fe-Nb-Zr Ternary System At 1,200 A Degrees C

Experimental Investigation on Isothermal Sections at 1273 and 1473 K in the Co–Ti–W System

Solidification and microstructure of ZA27/SiCp composite fabricated by mechanical-electromagnetic combination stirring process

Experimental determination of phase diagram in the Zn-Fe binary system