Abstract:Two semi-alicyclic thermoplastic polyimides (PI) have been prepared from stereoisomeric hydrogenated pyromellitic dianhydrides, including 1S,2R,4S,5R-hydrogenated pyromellitic dianhydride (ccHPMDA or H-PMDA) and 1R,2S,4S,5R-hydrogenated pyromellitic dianhydride (ctHPMDA or Hʹʹ-PMDA) and a fluorine-containing diamine, 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane (BDAF), respectively. The derived PI-1 (ccHPMDA-BDAF) and PI-2 (ctHPMDA-BDAF) resins were easily soluble in polar aprotic solvents, such as N -methyl-2-pyrrolidinone (NMP) and N,N -dimethylacetamide (DMAc) and meanwhile they also exhibited good thermoplasticities. Thus, the PI films (thickness: ~25 μm) and sheets (thickness: ~3 mm) were separately prepared from the PI solutions in DMAc and the PI powders, respectively. The stereoisomeric effects in the ccHPMDA-derived PI-1 and the ctHPMDA-derived PI-2 apparently affected the melt-flowability of the polymers. PI-2 exhibited lower melting viscosities than that of the PI-1 counterpart. The PI sheets exhibited obviously reduced optical transparency compared with those of the PI films; however better optical transparency than those of the common thermoplastic PI sheets. For example, PI-2 sheet showed the optical transmittance value at the wavelength of 760 nm (T 760 ) of 69.6%, which was 19.5% lower than that of the analogous PI-2 film (T 760 = 89.1%), however 50.3% and 65.7% higher than those of the commercially available PI-ref1 sheet (T 760 = 19.3%) derived from 3,3ʹ,4,4ʹ-oxydiphthalic dianhydride (ODPA) and 4,4ʹ-oxydianiline (ODA) and the PI-ref2 sheet (T 760 = 3.9%, Aurum ® PL450C, Mitsui Chem. Co, Ltd., Japan), respectively. Meanwhile, the PI-1 and PI-2 sheets showed the heat deflection temperatures (HDT) of 261.0 °C and 265.0 °C, respectively, which were obviously higher than those of the referenced PIs. At last, the PI sheets exhibited good mechanical properties, including high flexural strength (130.0 ~ 132.0 MPa), flexural modulus (2.87 ~ 2.96 GPa), compression strength (124.4 ~ 149.3 MPa), compression modulus (1.49 ~ 1.59 GPa), and impact strength (129.0 ~ 139.6 KJ/m 2 ).

Preparation and properties of rigid polyimide foams derived from dianhydride and isocyanate

Preparation and Dielectric Properties of Polyimide Foams Containing Crosslinked Structures

Preparation and Property of Polyimide Foams

Fabrication of rigid polyimide foams via thermal foaming of nadimide-end-capped polyester-amine precursor

Polyimide Foams with Ultralow Dielectric Constants

Studies on Polyimide Foams Prepared from Poly(Ester-amine Salt) Precursor Powder

Synthesis of poly(propylene glycol)-grafted polyimide precursors and preparation of nanoporous polyimides

Preparation and Properties of High-Temperature-Resistant, Lightweight, Flexible Polyimide Foams with Different Diamine Structures

Preparation of Open-Cell Rigid Polyimide Foam via Nonaqueous High Internal Phase Emulsion-Templating Technique

Closed-Cell Rigid Polyimide Foams for High-Temperature Applications: The Effect of Structure on Combined Properties

Novel Synthesis of Polyimide Foams with Aromatic and 1,6-Diaminohexane Imide Bonding

STUDY ON THE SYNTHESIS AND PROPERTIES OF POLYIMIDE FOAMS

Fabrication of Lightweight Polyimide Foams with Exceptional Mechanical and Thermal Properties

Synthesis and properties of fluorinated polyimides from 1,1-bis(4-amino-3,5-dimethylphenyl)-1-(3,4,5-trifluorophenyl)-2,2,2-trifluoroethane and various aromatic dianhydrides

Preparation and properties of semi-alicyclic thermoplastic polyimide sheets from stereoisomeric hydrogenated pyromellitic dianhydrides and fluorinated diamine

Synthesis and properties of polyimides from a diamine containing side diphenylphosphine oxide and trifluoromethyl groups

Fabrication of Rigid Isocyanate-Based Polyimide Foam Achieved Excellent Use Safety via Synergy between Expandable Graphite and Phosphorus-Containing Polyol

Fabrication of multifunctional polyimide foams with co-polymerized benzimidazole moieties for excellent thermal insulation and flame retardancy applications

Phenylethynyl-terminated Oligoimides Based on Bis(p-Aminophenoxy)dimethyl Silane: Effect of Siloxane Structure on Processability and Thermal Stability

Synthesis and Properties of a High‐molecular‐weight Poly(amic Acid) and Polyimide Based on 2,2‐Bis(3‐amino‐4‐hydroxyphenyl)hexafluoropropane

Dual Cross-Linked Networks Reinforced Polyimide Foams with Outstanding Piezoelectric Properties and Heat Resistance Performance