Abstract:Al-doped ZnO (ZAO) films, having film thickness of about 50–1200nm, were deposited at substrate temperature of 100–300°C by radio-frequency magnetron sputtering. Structural, electrical, and optical properties of as-deposited ZAO films have been studied as a function of film thickness and substrate temperature. The investigation of X-ray diffraction indicates that the crystalline quality of the film improves and its stress relaxes with increasing film thickness or substrate temperature, and preferred (002) orientation is found at substrate temperature above 100°C. By the observation under scanning electron microscope, columnar structure can be obviously observed from cross-section of the films with increasing film thickness at substrate temperature above 100°C; the surface morphology can exhibit nanocrystalline, honeycomb, or hillock structure, depending on film thickness and substrate temperature. Hall effect measurements reveal that the decrease of resistivity of the film is generally accompanied by the increase of carrier concentration and mobility with increasing film thickness or substrate temperature. It is speculated that the main scattering mechanism in as-deposited ZAO films is intercrystallite boundary scattering. The transmission spectra measurements of ZAO films indicate that average transmittance between 400 and 800nm decreases from about 86% to 70% with increase in film thickness. The obtained energy gap (Eg) of the films at different substrate temperatures is found in order of 200°C>300°C>100°C, which can be attributed to high carrier concentration and compressive stress at 200°C, but markedly low carrier concentration at 100°C. With increase in film thickness, the decrease in compressive stress and/or increase in crystallite size result in the decreased or unchanged tendency of Eg of the films although the carrier concentration increases.

Temperature-Dependant Growth and Properties of W-Doped Zno Thin Films Deposited by Reactive Magnetron Sputtering

Effect of Nucleation and Growth Kinetics on the Electrical and Optical Properties of Undoped ZnO Films

Effect of Reaction Temperature on Surface Morphology and Photoelectric Properties of ZnO Grown by Hydrothermal Method in Mixed Solvent

Research on WZO-TCO Thin Films Grown Via Reactive Electron Beam Vapor Deposition

Effects of Substrate Temperature on the Properties of N-doped P-Type ZnO Films Deposited by DC Reactive Sputtering

Temperature-dependent growth of zinc oxide thin films grown by metal organic chemical vapor deposition

STRUCTURAL AND OPTICAL STUDIES OF ZnO FILMS GROWN AT LOW TEMPERATURE

Influence of Deposition Temperature on the Crystallinity of Al-doped ZnO Thin Films at Glass Substrates Prepared by RF Magnetron Sputtering Method

Properties of boron-doped ZnO thin films deposited by pulsed DC magnetron sputtering at different substrate temperatures

Thickness Effect on Structure and Properties of ZAO Thin Films by RF Magnetron Sputtering at Different Substrate Temperatures

Effects of Substrate Temperature on the Properties of Mo-doped ZnO Films Prepared by RF Magnetron Sputtering

Dependence of electrical and optical properties of ZnO films on substrate temperature

Effect of substrate temperature on structural and electrical properties of K-doped p-ZnO thin films

Influences of Substrate Temperature on the Crystalline Characteristics and Optical Properties for ZnO Films Deposited on Freestanding Thick Diamond Films

Effects of substrate temperature on the properties of facing-target sputtered Al-doped ZnO films

Room temperature deposition of highly conductive and transparent H and W co-doped ZnO film

Substrate Temperature Dependence of the Properties of ZnO∶Al Thin Films Prepared by Mid-frequency Sputtering

Effects of deposition power and pressure on the crystallinity of Al-doped ZnO thin films at glass substrates by low temperature RF magnetron sputtering

Influences of Growth Temperature on the Crystalline Characteristics and Optical Properties for ZnO Films Deposited by Reactive Magnetron Sputtering

Temperature Effect on the Electrical, Structural and Optical Properties of N-Doped Zno Films by Plasma-Free Metal Organic Chemical Vapor Deposition

Room temperature deposition of highly conductive and transparent hydrogen and tungsten co-doped ZnO films for thin film solar cells applications