In-Situ Investigation on Tensile Deformation and Fracture Behaviors of Ti60 Alloy Rolled Sheet with Equiaxed Microstructure
Boning Wang,Weidong Zeng,Zibo Zhao,Runchen Jia,Jianwei Xu,Qingjiang Wang
DOI: https://doi.org/10.1016/j.jallcom.2022.166464
IF: 6.2
2022-01-01
Journal of Alloys and Compounds
Abstract:In this work, the deformation mechanism and fracture behavior of Ti60 alloy sheet with equiaxed microstructure (the volume fraction of equiaxed α grains is 68%) using the in-situ tensile test were studied by in-situ scanning electron microscope (SEM) and electron backscattering diffraction (EBSD). The results show that equiaxed α grains activate three coordinated deformation mechanisms, mainly single slip mode, supplemented by slip transfer and grain rotation. The alloy is mainly coordinated by equiaxed α grain deformation, dominated by prismatic< a> and basal< a> slip, and prismatic slip in (101̅0) plane and [12̅10] direction as the most active slip system. With the increase of deformation, the soft oriented equiaxed α grains preferentially occur prismatic slip, while some hard oriented grains rotate in the direction favorable to slip. When there is no slip transfer between adjacent grains, dislocation pile-up at the grain boundary and causes stress concentration, which makes the grain boundary easy to become the crack nucleation point. In SEM and EBSD studies, lamellar α grains have no obvious deformation characteristics. However, TEM study found that some lamellar α grains were kinked, which led to lamellar fracture and the formation of high-density dislocation areas around them. Meanwhile, due to the large difference in coordinated deformation ability between equiaxed α grains and lamellar α grains and between equiaxed α hard and soft oriented grains. Therefore, cracks are initiated, propagated and fractured mainly at the junction of the α colony composed of lamellar α grains and at the equiaxed α grain boundary.