Abstract:Fabricating chalcopyrite Cu(In,Ga)Se2 (CIGS) films from electrodeposition is one of the most effective ways to lower the production cost and energy consumption compared with that from vacuum methods. However, this process often produces a pronounced rough surface with impurity phases, induces the accumulation of gallium, and results in a low surface band gap. In this work, ammonium sulfide ((NH4)2S, AS) solution treatment is used as a single way to realize the optimization of the distribution of elements on the CIGS surface. It is revealed that this room-temperature process not only significantly reduces the surface roughness (Ra) but also incorporates sulfur (S) into the CIGS film successfully. An appropriate AS treatment duration can effectively remove the impurity phases and reduce the series resistance, and thus the dominant recombination moves from the CdS/CIGS heterojunction interface to the bulk. Consequently, the open-circuit voltage (VOC) and fill factor (FF) of solar cells have been greatly improved (from 484 to 532 mV, from 62.52 to 68.15%), leading to higher efficiency of 11.92%. This work focuses on revealing the etching mechanism of the CIGS films by the AS treatment at room temperature.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c00220?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c00220</a>.Best solar cell parameters of different unannealing samples (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c00220/suppl_file/ae1c00220_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Fabrication and Centeracterization of Ordered CuIn (1− X ) Ga X Se 2 Nanopore Films Via Template-Based Electrodeposition

Increasing surface band gap of Cu(In,Ga)Se2 thin films by post depositing an In-Ga-Se thin layer.

Self-assembled Synthesis of 3D Cu(In1 − Xgax)se2nanoarrays by One-Step Electroless Deposition into Ordered AAO Template

Fabrication of Cu(In,Ga)Se-2 Thin Films from Nanoparticles by Non-Vacuum Mechanochemical Method and Rapid Thermal Annealing Process

Synthesis and Characteristics of Cu(In,Ga)Se2 Thin Films from Nanoparticles by Solvothermal Method and Selenisation Process

Formation of CuInSe2 and Cu(In,Ga)Se2 films by electrodeposition and vacuum annealing treatment

Research progress on synthesis of CuIn1-x Gax Se2 nanoparticles

Research progress on synthesis of CuIn 1-xGa xSe 2 nanoparticles

Metal Precursor with Bi-Layer Indium for Cu(In,Ga)Se2 Thin Film Preparation

Preparation of Cu(In,Ga)Se2 Thin Film by Solvothermal and Spin-coating Process

Metal Precursor Influence On Performance Of Cuin1-Xgaxse2 Films

Synthesis and Characterization of CIGS Powder

Influence of Bilayer Precursor Films on Structure and Morphology of CIGS Films

Preparation And Characterization Of Cu(In,Ga)Se-2 Thin Films By Selenization Of Cu0.8ga0.2 And In2se3 Precursor Films

Preparation of Cu(In,Ga)Se2 Thin Film by Non-Vacuum Mechanochemical and Spin-Coating Process

Metal Precursor Influence on Performance of Culn1−xGaxSe2 Films

Growth and Characterization of Copper Indium Gallium Diselenide Films for Solar Cells Fabrication

Investigation of Cu(In,Ga)Se2 Polycrystalline Growth: Ga Diffusion and Surface Morphology Evolution

Preparation and layer-by-layer solution deposition of Cu(In,Ga)O2 nanoparticles with conversion to Cu(In,Ga)S2 films

One-step electrodeposition of CuInxGa1−xSe2 thin films from a mixture system of ionic liquid and ethanol

Enhancing Surface Properties for Electrodeposited Cu(In,Ga)Se 2 Films by (NH 4 ) 2 S Solution at Room Temperature