Preparation of High-Purity Sponge Bismuth from Copper Converter Flue Dusts by Hydrometallurgical Process

廖婷,陈白珍,陈亚

DOI: https://doi.org/10.3969/j.issn.0258-7076.2012.06.021

2012-01-01

Abstract:The process of "acid leaching-bismuth precipitation-dearsenication-replacement" was used for preparation of high-purity sponge bismuth from copper converter flue dusts. Firstly, 0.5 mol·L-1 H2SO4 solution was used as leaching agent, under the condition of 60°C water bath, the liquid-solid ratio 2:1, leaching 3 h, so that most solubility element such as Zn, Cd, Cu, Fe could be separated and bismuth get enrichment. Secondly, H2SO4-NaCl blend solution was used as leaching agent for the second leaching process to leaching the once acid leaching residue, and the operation conditions of the second leaching process were optimist. The results showed that a counter-current circulation leaching under the condition of 60°C water bath, 2 mol·L-1 H2SO4, 2.5 mol·L-1NaCl, and the liquid-solid ratio 2:1, was feasible, and the average extraction rate of bismuth reached 95.2%, while the leaching solution concentration of bismuth was 15.88 g·L-1. By adjusting pH of leaching solution from 0.5 to 3.0 with ammonia, over 96% of bismuth was selectively recovery as including bismuth precipitation and separated from element such as Cu, Sib, BP, while the precipitation contents 36.2% Bi and 19.1% As. Since the bismuth grade was low, arsenic content was too high in the precipitation, 2 mol·L-1 Noah was used as arsenic removing agent for 30 min, arsenic removal rate reached 97.05%, and bismuth grade increased to 57.28%. Bismuth materials after dearsenication dissolved by nitric acid, and then replacement of sponge bismuth by iron powder, 98% bismuth could be replaced, while the sponge bismuth purity was as high as 90% above.