Abstract:By employing an in-situ reaction pressureless sintering method, self-reinforced and SiC-B4C-ZrB2 multiphase composites were successfully prepared. The effect of TiO2 and ZrO2 additions on the sintered density, microstructure, and mechanical properties of the composites was investigated. TiO2 and ZrO2 were completely transformed into TiB2 and ZrB2 phases during the sintering process, and their appropriate addition helped enhance the relative density of the composites. In the SiC-B4C-TiB2 (SBT) composite, the introduction of TiB2 facilitated grain growth in all phases. The composite with 12 vol% TiB2 (SBT12) exhibited optimal mechanical properties, with Vickers hardness, fracture toughness, and flexural strength reaching 30.1±0.8 GPa, 5.17±0.23 MPa·m1/2, and 491±24 MPa, respectively. In the SiC-B4C-ZrB2 (SBZ) composite, the presence of ZrB2 resulted in the formation of a ternary eutectic liquid phase, SiC-B4C-ZrB2, during the sintering process, leading to grain coarsening and the generation of plate-like SiC grains. Among them, the composite with 6 vol% ZrB2 (SBZ6) demonstrated the best overall performance, with Vickers hardness, fracture toughness, and flexural strength of 29.7±0.6 GPa, 6.17±0.36 MPa·m1/2, and 443±22 MPa, respectively. Additionally, SBZ9 exhibited the highest fracture toughness, reaching 6.43±0.44 MPa·m1/2, with the pull-out of plate-like grains considered as the primary contributing factor. This study provides a reference for the preparation of high-strength and tough SiC-B4C-MeB2 multiphase composites through low-temperature pressureless sintering.

Inhibiting Effect of Additives on Formation of ZrC Phase in ZrB2–BN Composites by Reactive Hot Pressing

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Microstructure and Mechanical Properties of Reactive Hot-Pressed BN-ZrB_2-ZrO_2 Composites

Reactive Hot Pressing and Sintering Characterization of ZrB2–SiC–ZrC Composites

Reactive sintering behavior and enhanced densification of (Ti,Zr)B2–(Zr,Ti)C composites

Reactive hot pressing of ZrB2-SiC composites

Densification, microstructure and mechanical properties of ZrB2–SiCw ceramic composites

Role of h-BN content on microstructure and mechanical properties of hot-pressed ZrB2–SiC composites

The Effect of Tio2 and Zro2 Additives on the Density, Microstructure, and Mechanical Properties of Pressureless Sintered Sic-B4c

Microstructure, mechanical properties and thermal shock resistance of hot-pressed ZrO2(3Y)-BN composites

High-pressure synthesis of Al<sub>2</sub>O<sub>3</sub>-cBN composites: Effect of thermodynamic condition and cBN volume fraction on their microstructure and properties

Effect of ZrO2 content on microstructure, mechanical properties and thermal shock resistance of (ZrB2+3Y-ZrO2)/BN composites

Effect of Ti Additives on the Sintering Behavior and Mechanical Properties of ZrC-W Composites

Microstructure and Mechanical Properties of ZrB2-SiC Composites

Beneficial effect of low BN additive on densification and mechanical properties of hot-pressed ZrB2–SiC composites

Microstructure and mechanical properties of hot pressed ZrC-SiC-ZrB 2 composites

Effect of Iron Additive on the Sintering Behavior of Hot-Pressed ZrC-W Composites

STUDY ON THE STRUCTURE OF TiB2-ZrB2 COMPOSITES PREPARED BY HOT PRESSING

Low-Temperature Sintering Behavior and Mechanical Properties of Bn-Zro2-Sic Composites

Mechanical Properties and Microstructure of in Situ Synthesized ZrB 2 -Zrn 1− X Composites

Microstructural Features and Mechanical Properties of ZrB2–SiC–ZrC Composites Fabricated by Hot Pressing and Reactive Hot Pressing