Effects of La on As-Cast Microstructure and Mechanical Property of ZK60 Alloy

Zhenghua Huang,Wenjun Qi,Kaihong Zheng,Xinming Zhang,Min Liu,Zhiming Yu

DOI: https://doi.org/10.3969/j.issn.0258-7076.2012.05.027

2012-01-01

Abstract:Magnesium alloys were used widely in automotive, communication, electronic and aerial industries, but their mechanical properties at ambient and elevated temperatures should be enhanced further. Microstructures and phase compositions of as-cast ZK60-xLa (x=0~3) magnesium alloys were analyzed by optical microscope, scanning electron microscope, X-ray diffraction and differential scanning calorimetry. Meanwhile, the hardness and tensile mechanical property were tested. The results showed that as-cast microstructure was refined gradually with increasing the La content. MgZn 2 phase with low melting point gradually decreased to disappear, while τ 1-Mg 42Zn 53La 5 new phase with high melting point increased gradually. Meanwhile, second phase was inclined to distribute along grain boundary by continuous reticulation. Hardness HV exhibited peak values at low and high La contents, respectively. With increasing the La content, tensile strength σ b and elongation δ at ambient temperature decreased gradually from 225 MPa and 9% for ZK60 alloy to 137 MPa and 1.5% for ZK60-3.04La alloy, respectively. Tensile fracture changed from the complex mode of ductile fracture and brittle fracture to single brittle fracture. However, the addition of La could enhance the tensile mechanical property at elevated temperature effectively. At ambient temperature, ZK60-1.03La alloy exhibited lower value of σ b by 25 MPa than ZK60 alloy. At 423 K, σ b was reduced to 181 and 174 MPa for ZK60-1.03La and ZK60 alloys, respectively, which led to higher value of σ b by 7 MPa for the former alloy. At 448 K, σ b was further reduced to 168 and 150 MPa for the two alloys, respectively, where the gap reached 18 MPa. Only τ 1-Mg 42Zn 53La 5 phase with high thermal stability existed among the microstructure of ZK60-1.03La alloy, which could pin the grain boundary and hinder its sliding at elevated temperature effectively.