Decarbonization and Its Improvement of Coarse-Grained Low Cobalt Cemented Carbide Sintered by Microwave Irradiation

BAO Rui,YI Jian-hong,YANG Ya-jie,PENG Yuan-dong,ZHANG Hao-ze,LOU Jing

DOI: https://doi.org/10.3969/j.issn.1673-0224.2012.02.006

2012-01-01

Abstract:Result indicates that decarbonization phenomenon always exists when coarse grain WC-Co cemented carbide is prepared by conventional microwave irradiation,which leads to the core-shell structure owing to different microstructure between the surface and central area.The mechanical properties of the alloy are adversely affected by this special structure.In order to avoid the formation of the decarbonization phase η,i.e.W3Co3C phase,88%WC-12%Co(YG12) and 94%WC-6%Co(YG6) cemented caribde were prepared and carbon black was added when milling raw powders.The results show that the transverse rupture stress(TRS) of YG12 and YG6 can reach 3 109 MPa and 2 642 MPa,respectively;hardness rockwell A(HRA) of them can reach 88.7 and 89.8,respectively when added carbon black content is mass fraction of 0.2%,and an uniform microstructure between the surface and central area of WC-Co alloy with no η(W3Co3C) can be obtained.However,the TRS and hardness of the alloys will decrease because of a large number of graphite phase were separated out from alloy when the added carbon content is more than 0.2%.When added carbon content is 0.4%,the TRS of YG12 and YG6 are only 2 465 MPa and 2 213 MPa,respectively.