Synergistic Effects of Multicomponents Produce Outstanding Soot Oxidation Activity in a Cs/Co/MnO x Catalyst
Meng Wang,Yan Zhang,Yunbo Yu,Wenpo Shan,Hong He
DOI: https://doi.org/10.1021/acs.est.0c06082
2020-12-18
Abstract:The control of soot emission from diesel vehicles is of extraordinary importance to the environment, and catalytic removal of soot is a highly effective and clean method. Here, we report a novel, non-noble metal catalyst for application in the catalytic combustion of soot with superb activity and resistance to H<sub>2</sub>O and SO<sub>2</sub>. MnO<i><sub>x</sub></i> oxide was prepared <i>via</i> a hydrothermal method, and then, Cs and Co were loaded on MnO<i><sub>x</sub></i> by impregnation. The 5%Cs/1%Co/MnO<i><sub>x</sub></i> catalyst displayed excellent catalytic activity with values of <i>T</i><sub>10</sub> (332 °C), <i>T</i><sub>50</sub> (371 °C), and <i>T</i><sub>90</sub> (415 °C) under loose contact. The as-prepared catalysts were investigated by X-ray powder diffraction (XRD), transmission electron microscopy (TEM), H<sub>2</sub> temperature-programmed reduction (TPR), O<sub>2</sub> temperature-programmed desorption (TPD), X-ray photoelectron spectroscopy (XPS), and X-ray absorption fine structure (XAFS). The results suggest that, after the introduction of Cs and Co into the MnO<i><sub>x</sub></i> oxide, more NO<sub>2</sub> molecules take part in soot oxidation, exhibiting higher NO<sub>2</sub> utilization efficiency; this is due to the synergistic effects of multiple components (Cs, Co, and Mn) promoting the generation of more surface-active oxygen and then accelerating the reaction between NO<sub>2</sub> and soot. This study provides significant insights into the development of high-efficiency catalysts for soot oxidation, and the developed 5%Cs/1%Co/MnO<i><sub>x</sub></i> catalyst is a promising candidate for application in diesel particulate filters.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.est.0c06082?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.est.0c06082</a>.Summary of characterization and catalytic activity tests of catalysts: soot oxidation activity; XRD results of the spent 5%Cs/1%Co/MnO<i><sub>x</sub></i> catalyst; HRTEM images and Mn 2p XPS of the as-prepared catalysts; Mn 3s, Mn 2p, and O 1s XPS results of the spent 5%Cs/1%Co/MnO<i><sub>x</sub></i> catalyst; relationship between the H<sub>2</sub> consumption amounts and <i>T</i><sub>50</sub>; NO<sub>2</sub> profiles; relationship between surface-active oxygen obtained from O<sub>2</sub>-TPD and the NO<sub>2</sub> utilization efficiency; BET surface areas, XRF, and curve-fitting results of Mn-K EXAFS for different samples; and the NO<sub>2</sub> utilization efficiency(<a class="ext-link" href="/doi/suppl/10.1021/acs.est.0c06082/suppl_file/es0c06082_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
environmental sciences,engineering, environmental