Abstract:A large thermal gradient about 190 degrees C/cm was established in the thickness direction of preform and the cylindrical carbon/carbon composites with radial gradient pyrocarbon (PyC) PyC ) distribution were rapidly prepared via the cooling pyrolysis technology in the high temperature surface based on the large thermal gradient chemical vapor infiltration ( CPTHTS-LTGCVI ). The decrease of initial temperature and the increase of cooling rate both contribute to the opening of closed pore and pore expansion, which are conducive to improving the densification degree. Moderate initial temperature (about 1130 degrees C) and cooling rate (10 degrees C/5 h) are optimal to rapidly preparing C/C composites with good density uniformity. For the whole cylindrical C/C composites, the faster the cooling rate, the higher the density and density uniformity, the fewer the super macropores. As the cooling rate is 10 degrees C/2.5 h, the density of sample can reach 1.57 g/cm3 3 within 50 h, and the carbon yield in the first stage and accumulation can reach 84 % and 50 %, respectively. From the inner wall (IW) IW ) to the outer wall (OW), OW ), there are three successive regions about RL , RL+SL + SL and SL PyC with gradually weakened texture, which is related to the insufficient pyrolysis caused by the decreased temperature and increased concentration, and the aromatization caused by the extended gas retention time. The edge dislocations and non-coherent sub-grain boundaries of PyC may be related to the distorted aromatic carbon planes containing five-membered rings. The edge dislocations may be the main reason of texture reduction and structural evolution of PyC. .

Density, Microstructure and Mechanical Property of Large-Scale C/C Composites Prepared by Thermal Gradient Cvi

Density, microstructure and property of large-scale carbon/carbon composites prepared by fast thermal gradient cvi

Densification Behavior of Thermal Gradient Cvi of Large-Scale C/C Composites

Preparation and Properties of Density Gradient Carbon/Carbon Composites

Preparation for 2D–C/C composites with pure RL textures and its characteristic

Microstructure and Mechanical Properties of Multilayer-textured 2D Carbon/Carbon Composites

Preparation and Mechanical Properties of Carbon/carbon Composites with High Textured Pyrolytic Carbon Matrix

Study on the Mechanism of Rapid Densification and Structural Evolution of C/C Composites by Cooling Pyrolysis

Fracture Mechanism of 2D-C/C Composites with Pure Smooth Laminar Pyrocarbon Matrix under Flexural Loading

Fast Densification Study of C/C Composites with Multi-Coupling Fields CVI

Microstructure and Mechanical Properties of C/C Composites with Gradient Distributed TaC Interlayer

Bending Properties and Fracture Mechanism of C/C Composites with High Density Preform

Dependence of Mechanical Properties on Microstructure of High-Textured Pyrocarbon Prepared Via Isothermal and Thermal Gradient Chemical Vapor Infiltration

Effects of Carbon Fiber Architecture on the Microstructure and Mechanical Property of C/C-SiC Composites

The distribution of microstructure and mechanical properties of carbon-carbon composites

Study on Microstructure and Mechanical Properties of Carbon/Carbon Composite Obtained by Chemical Vapor Infiltration

Process and Properties of C/C Composites by Chemical Liquid-Vaporized Infiltration

Preparation of C/C Composites by Thermal Gradient Chemical Vapor Infiltration with Vaporized Kerosene As a Precursor

Densification Behavior and Microstructure of Carbon/carbon Composites Prepared by Chemical Vapor Infiltration from Xylene at Temperatures Between 900 and 1250 °C

Carbon/carbon composites preparation by novel technology and its characteristic

Rapid Densification of Carbon/Carbon Composites Plate by Pressure‐Gradient Chemical Vapor Infiltration