Abstract:To develop the full application potential of composite materials, research on the post-buckling behavior of composite stiffened panels is of great significance. In this paper, the impact and compression after impact (CAI) behaviors of four different types of composite stiffened panels were studied by numerical simulation and experimental methods. The low-velocity impact damage simulated dynamically was introduced as the initial state in the compression simulation, and a two-dimensional shell model with Hashin failure criteria and stiffness degradation was adopted to estimate the failure load of composite stiffened panels under impact and CAI. The error between simulation results and test results was less than 10%, showing that the method used in this study achieved considerable accuracy in experimental results. Analysis of the impact test results revealed that the extent of damage is related to many factors, including the cross-sectional size of stiffeners, the spacing of stiffeners, and the material and thickness of the skin. In addition, the influence of fatigue damage on residual strength after impact was also studied experimentally, with results showing that the buckling and failure loads decreased by about 5% under 106 flight fatigue loads. However, there were obvious fluctuations in the load-displacement curves, which may have been caused by debonding between the stiffeners and the skin. Experimental results and the simulation matrix show that the post-buckling ratio increased with the increase of the stiffness ratio, then was stable after 2.0. Furthermore, the thinner the skin, the greater the post-buckling ratio. The experimental and simulation results provide an important reference for the structural design and failure-mechanism analysis of composite stiffened panels.

STUDY ON COMPRESSIVE PROPERTIES OF Z-REINFORCED STIFFENED COMPOSITE PLATE WITH DISCRETE-SOURCE DAMAGE

Concurrent Multiscale Modeling of In-Plane Micro-Damage Evaluation in Z-pinned Composite Laminates

Micro-damage Initiation Evaluation of Z-Pinned Laminates Based on a New Three-Dimension RVE Model

Effect of Ø 0.11 Mm Z-pinning on the Properties of Composite Laminates Via an Ultrasound Guided Insertion Process

Strengthening of Composite T-joints Using Ø 0.11 Mm Z-pins Via an Ultrasound-Guided Insertion Process

Design and optimization of composite sub-stiffened panels

Experimental and Numerical Study on Failure Behaviors of Composite Grid Stiffeners under Tensile and Flexural Loading

Experimental Investigation of Z-pin Insertion Angles on the Mechanical Behavior and Failure Mechanism of Compression after Impact for CFRP Laminates

Cracking Behavior of Cfrp Laminate-Strengthened Rc Beams with Premechanical and Postmechanical Environmental Damage

Computational modelling of postbuckling behavior of composite T-stiffened panels with different bonding methods

Numerical and experimental investigation of pre-damaged composite stiffened panel under axial compression

An Experimental and Numerical Study on Impact and Compression after Impact of Stiffened Composite Panels

Investigation of the out-of-plane load-bearing capacity of T1100/5405 composite T-stiffened panels

A Novel Methodology to Research the Residual Compressive Mechanical Properties of Composite Stiffened Panel after Low Velocity Impact Based on Quantification Damage Simulation

A study on low-velocity impact damage of Z-pin reinforced laminates

Investigation on damage behavior of composite T-shaped stiffened panels under compression after multi-point impact considering impact positions

Experimental and Numerical Analysis for the Post-Buckling Behavior of Stiffened Composite Panels with Impact Damage

Effect of fine metallic Z-pin on compressive property of open-hole composite laminate

Experimental and numerical investigation of damage evolution in carbon fiber reinforced polymer stiffened panel in post-buckling regime

Experimental Investigation of Shear Fatigue Behavior of Composite Stiffened Panels with Impact Damage

THE STUDY ON TESTS AND NUMERICAL SIMULATION OF CRACK PROPAGATION PROBLEM IN DELAMINATION FAILURE OF COMPOSITE LAMINATED PLATE