Abstract:Abstract Metal magnesium is mainly produced from the calcined dolomite by the silicothermic production. However, in this process, the reduction temperature is higher while the reaction speed is slow, which results in higher energy consumption and serious environmental problems. In this paper, adding aluminum into the ferrosilicon reducing agent is expected to lower the reaction temperature so as to solve the problems above. The phase transition involved in the whole reduction process including with and without aluminum addition were investigated in details by theoretical calculation and experimental research. The influence of aluminum on the magnesium oxide reduction path was analysis to clarify the internal mechanism. The results show that aluminum added into the ferrosilicon would first react with magnesium oxide to form magnesium vapor and alumina under vacuum pressure of 10 Pa when the temperature rises to 720°C. Then, calcium aluminate would be formed by the reaction of aluminum oxide and calcium oxide. Once the temperature reaches 1150°C, silicon begins to reduce the magnesium oxide to create the silicon oxide that will finally react with calcium oxide to form calcium silicate. When the temperature rises above 1150°C, both the aluminum and silicon will participate in the reduction of magnesium oxide. In the process of heating up, the mixture of aluminum, ferrosilicon and calcined dolomite forms Mg 2 Al 4 Si 5 O 18 and Ca 3 Al 2 (OH) 12 phase with the components in calcined dolomite. Mg 2 Al 4 Si 5 O 18 and Ca 3 Al 2 (OH) 12 phase finally form Ca 12 Al 14 O 33 phase. The interaction between aluminum and ferrosilicon in the mixture is less; the mixture of aluminum and ferrosilicon first forms Al 3 FeSi 2 phase, and finally has the trend of forming Al 4.5 FeSi phase. There is a great difference between the phase transformation of aluminum in the mixture of aluminum, ferrosilicon and calcined dolomite and that of aluminum in the mixture of aluminum and ferrosilicon.

Phases Transformation of Boron Mud During Carbothermal Reduction Process

Phase Analysis of Forsterite in Carbothermal Reduction Processing

Phase Behavior of Silica Brick Used in Carbothermal Reduction

Phase Behavior Analysis of Low-Grade Bauxite and Rutile by Carbothermal Reduction-Nitridation

Phase behaviors of talc minerals in carbothermal reduction process

Phase transformation of high aluminium fly ash in carbothermal reduction–nitridation at high temperatures

Reduction Kinetics and Microscopic Properties Transformation of Boron-Bearing Iron Concentrate–Carbon-Mixed Pellets

Evolution of Coke Microstructure and Metallurgical Properties During Graphitization in a Blast Furnace

Phases transformation of high-alumina fly ash under carbothermal reduction and nitridation

Phase behavior analysis of MgO–C refractory at high temperature: Influence of Si powder additives

Phase transformation of MgAl2O4 -SiAlON composites synthesized by carbonthermal reduction and nitridation method from magnesite and bauxite

Carbothermal reduction of red mud for iron extraction and sodium removal

Carbothermic Reduction of Mullite at Elevated Temperature

Phase transformation involved in the reduction process of magnesium oxide in calcined dolomite by ferrosilicon with additive of aluminum

Phase Transformation Of Diatomite During Magnesiothermic Reduction Process

Effects of CaO Additives on the Phase Evolution of ZrO2-SiC Composites from Zircon by Carbothermal Reduction

Effect of Temperature on the Phase Behaviors of Zircon by Carbothermal Reduction-Nitridation

Preparation Of Al2o3-Sic Composite Powder From Kyanite Tailings Via Carbothermal Reduction Process

The Phase Transformation of Baiyunebo Iron Ore Treated with Reductant Sintering

Influences of Carbon Contents on the Products of Carbothermal Reduction-nitriding of Natural Quartz

Carbothermal/aluminothermic Reduction Nitridation Synthesis of ZrN–SiAlON Refractory Composites from Zircon and Bauxite: a Comparative Study of the Reduction Effect of Reducers