Abstract:A novel ternary eutectic salt KNO3-NaNO2-KNO2 (KNK) was designed and prepared for thermal energy storage (TES) in a concentrating solar power system (CSP). The thermo-physical properties of KNK such as melting point, decomposition temperature, fusion enthalpy, density, viscosity, thermal conductivity and specific heat capacity were determined respectively. Furthermore the thermal energy storage capacity was evaluated and discussed. Then a comparison of the thermo-physical properties between commercial Hitec and KNK was carried out. KNK showed smaller density, lower viscosity, slightly smaller thermal conductivity, much higher specific heat capacity and bigger thermal energy storage capacity. Raman spectrum displayed that the N-O of NaNO2 frequency peak at about 820 cm−1 in KNK had more significant shift, which could be attributed to a stronger interaction between Na+ and NO2−. Scanning electron microscope (SEM) showed K and Na elements of Hitec were uniformly distributed, while K and Na elements of KNK were in complementary distribution which could be caused by stronger repulsion between Na+ and K+. It was concluded that the stronger interaction and repulsion were correlated to the higher specific heat capacity. Molecular dynamics (MD) simulation was performed to explore the different macroscopic properties of two molten salts from the perspective at molecular level. The characterizations of radial distribution functions (RDF), coordination number and angular distribution functions (ADF) suggested that the interaction between Na+ and NO2− is stronger and that the arrangement of ion clusters was looser in KNK. The results were in good agreement with the analysis of Raman spectrum and SEM.

PREPARATION AND EXPERIMENTAL STUDY OF BINARY NITRATE SALTS

Experimental Study On Thermal Performance Of Mixed Nitrate And Carbonate Salts

Thermal stability of sodium nitrate–sodium nitrite melts: A Raman spectra study

Preparation and Thermal Properties of Quaternary Mixed Nitrate with Low Melting Point

Study on preparation and thermal properties of mixed chloride salts

Investigation on thermal performance of eutectic binary nitrate-carbonate molten salt under thermal shock condition

Enhancing phase change thermal properties of unitary and binary nitrates by carbon/ceramic-based nanoparticles via interfacial effect

Preparation And Experimental Study Of Mixed Carbonates With High Maximum Using Temperature

Study on the preparation and thermal properties of binary mixed chloride salts

Thermophysical Properties' Enhancement of LiNO3-NaNO3-KNO3-NaNO2-KNO2 Mixed with SiO2/MgO Nanoparticles

Novel high specific heat capacity ternary nitrate/nitrite eutectic salt for solar thermal energy storage

Preparation, crystallographic feature, synthon investigation and Hirshfeld surface analysis of both 3D supramolecular anhydrous organic salts constructed by triphenylmethylamine, 3-nitrophthalic acid and 5-nitroisophthalic acid

Solubility, correlation, Hansen solubility parameter and thermodynamic analysis of 2,4-dinitroanisole in three binary mixed solvents

Electrochemical Study on the Impact of Nacl Impurity on Corrosion of Stainless Steel 316l in Molten Nitrate Salts for Thermal Energy Storage

Synthetic Test of Bisquaternary Ammonium Salt BQAS

Measurement and Correlation of Solubility of Thiamine Nitrate in Three Binary Solvents and Thermodynamic Properties for the Solutions in Different Binary Mixtures at (278.15–313.15) K

Preparation of FLiNaK molten salt

Probing Thermal Decomposition Mechanism of Molten Nitrite/nitrates Salt by Time of Flight Mass Spectrometry

Phase diagram thermodynamic calculation of KNO3-NaNO2-KNO2 ternary system molten salt and its thermophysical properties investigation for thermal energy storage

Synthesis and investigation of 5-amino-2,4,6-trinitrobenzene-1,3-diol and its salts

Thermal Characterization of [C2Im][NO3] and Multivalent Nitrate Salts Mixtures