Abstract:ZrN–Si3N4 composite powders were synthesised from natural zircon and quartz via carbothermal reduction and nitridation reaction. The effects of various raw material compositions and heating temperatures on phase transformation and product morphologies under flowing nitrogen atmosphere were investigated by X-ray diffraction, scanning electron microscopy and energy dispersive spectroscopy. The phase equilibrium relationships of the ZrO2–SiO2–C–N2 system at different heating temperatures were also investigated based on the thermodynamic analysis. Products with different phase compositions and morphologies were obtained at different conditions. The products were composed of ZrN, β-Si3N4 and a small amount of c-ZrO2 by carbothermal reduction and nitridation of zircon with less than 20wt.% quartz. With 30wt.% quartz, granular ZrN as well as columnar and acicular β-Si3N4 were detected in the products. With 40wt.% or 50wt.% quartz, the products consisted of ZrN, β-Si3N4, Si2N2O, c-ZrO2 and m-ZrO2. The optimum quartz content for synthesizing ZrN–Si3N4 composite powders was 30wt.%. At heating temperatures below 1600°C, the products were composed of ZrN, β-Si3N4, β-SiC, Si2N2O, m-ZrO2 and c-ZrO2.

Phase Behavior of Serpentine Mineral by Carbothermal Reduction Nitridation

Synthesis of Sialon-SiC Composites from Kyanite Tailings by Carbothermal Reduction Nitridation

Synthesis of β-Si3N4 powder from quartz via carbothermal reduction nitridation

Phase behaviors of talc minerals in carbothermal reduction process

Phase Behavior of Silica Brick Used in Carbothermal Reduction

Phase Behavior Analysis of Low-Grade Bauxite and Rutile by Carbothermal Reduction-Nitridation

Synthesis of Si 3 N 4 powder with tunable α/β-Si 3 N 4 content from waste silica fume using carbothermal reduction nitridation

Effect of Temperature on the Phase Behaviors of Zircon by Carbothermal Reduction-Nitridation

Synthesis of TiN-Si3N4 Composites from Rutile and Quartz by Carbothermal Reduction Nitridation

Influence of Sintering Temperature on Phase Behavior of Products from Rutile and Quartz by Aluminothermic Reduction Nitridation

Phase transformation of high aluminium fly ash in carbothermal reduction–nitridation at high temperatures

Synthesis of ZrN–Si3N4 composite powders from zircon and quartz by carbothermal reduction and nitridation

Synthesis of well-dispersed β-Si3N4 with equiaxed structures using carbothermal reduction–nitridation method

Synthesis of Β-Sialon/ti(c,n) Composites Using Low and Middle Grade Bauxite and Ilmenite by Carbothermal Reduction-Nitridation

Synthesis of ZrN-sialon composites from zircon and alumina by carbothermal reduction-nitridation

Phase transformation of MgAl2O4 -SiAlON composites synthesized by carbonthermal reduction and nitridation method from magnesite and bauxite

Influences of Carbon Contents on the Products of Carbothermal Reduction-nitriding of Natural Quartz

Preparation of Sialon/Si3N4-SiC Composite Refractories Using Kyanite Tailings

Carbothermal/aluminothermic Reduction Nitridation Synthesis of ZrN–SiAlON Refractory Composites from Zircon and Bauxite: a Comparative Study of the Reduction Effect of Reducers

Synthesis of Ti(C,N) Powder Via CRN Method from Rutile/Carbon Mixtures

Preparation of Sialon/Si<sub>3</sub>N<sub>4</sub>-SiC Composite Refractories Using Kyanite Tailings