Abstract:Intermetallics combining metal and ceramic properties exhibit colorfully complicated growth morphologies in solidification. Different from the solidus phase solidification, intermetallic solidification remains less understanding of the correlation between processing parameters and microstructure morphologies. In this paper, considering that; the intermetallic compound Al2Cu phase has well-known thermophysical properties available for the theoretical and experimental research, we carried out the directional solidification experiments and focused on an Al-Al2Cu hypereutectic alloy, where the Al2Cu phase was solidified as a primary phase. The primary Al2Cu phase growth behavior in the experiments included phase competition growth between coupled eutectic and primary phase, faceted phase transition and its change in growth morphology. By using a high thermal gradient directional solidification apparatus, the directionally solidified microstructures of Al-40%Cu (mass fraction) hypereutectic alloy were investigated and discussed based on the competition growth model. As the growth rate was changed abruptly from 10 mu m/s to 2 mu m/s, the microstructure transition from a primary Al2Cu dendrite plus interdendritic eutectic to an entirely coupled eutectic occurred due to the interface growth temperature of the coupled eutectic exceeding that of the primary Al2Cu dendrite. Also, the alloy liquid composition ahead of the solid/liquid interface approaching the eutectic point caused this microstructure transition. Simultaneously, in the changing growth rate experiments. the primary Al2Cu dendrites were firstly broken into small ones and then became the eutectic microstructure; it was interpreted rather by the decrease in liquid solute concentration ahead of the solid/liquid interface than by the effect of the thermal-solutal convection. Moreover, the morphology change in phase growth from faceted primary Al2Cu phase to non-faceted phase was observed by reducing abruptly the growth rate from 10 mu m/s to 2 mu m/s, which can be explained by the Jackson factor alpha decreasing with increasing the interface growth temperature of primary Al2Cu phase.

Three-Dimensional Microstructure Reconstruction and the Eutectic Spacing Adjustment During Directional Solidification of Al-40%Cu Hypereutectic Alloy

Effect Of Directional Solidification Rate On Microstructure And Orientation Of Hypereutectic Al-Al2cu Alloy

Analysis on Microstructure of Al-40%Cu Alloy in Directional Solidification Process

EFFECT OF AN ABRUPT GROWTH RATE ON PRIMARY Al_2Cu PHASE IN DIRECTIONAL SOLIDIFICATION OF Al-40%Cu HYPEREUTECTIC ALLOY

Ultrasonic Solidification and Microstructural Evolution of Binary Al-12.6%Si Eutectic Alloy

Ternary Eutectic Growth During Directional Solidification of Ag–Cu–Sb Alloy

Microstructure Evolution and Orientation Analysis of Hypereutectic Al-Al2cu Alloy under Directional Solidification

Study on the Directional Solidification of Hypereutectic Cu-Cr Alloy

Modulating Phase Constitution and Copper Microsegregation for FeCoNiCuAl High-Entropy Alloy by Optimized Ultrasonic Solidification

Phase Constitution and Microstructure Evolution of Rapidly Solidified Ti-Cu-Fe Alloy

Formation Mechanism of Ternary NiAl-Mo Eutectic Alloy under Quenching Condition

Microstructure Evolution of Directionally Solidified Al-12%Ni Hypereutectic Alloy

Band-Like Micro Structures and Formation Mechanism in Directionally Solidified Cu-1.0%Cr Alloy

Directional Solidification Microstructures of Cu-55Sn Hypo-peritectic Alloy

Effect of thermosolutal convection on microstructure of directionally solidified Al-Al2Cu hypereutectic alloy

Microstructure Evolution of Cu-1.0% Cr Hypoeutectic Alloy During Directional Solidification

Forming Mechanism of α-Phase in Directionally Solidified Microstructure of Hypereutectic Cu-Cr Alloy

Microstructure Evolution and Growth Behaviors of Faceted Phase in Directionally Solidified Al-Yalloys I. Microstructure Evolution of Directionally Solidified Al-15%Y Hypereutectic Alloy

Study on the in Situ Composites Microstructure of the Directionally Solidified Hypoeutectic Cu–Cr Alloys

Effect of Sample Size on Intermetallic Al2Cu Microstructure and Orientation Evolution During Directional Solidification

Microstracture and Interface Morphology of Cu-1.0Cr Alloy in the Non-steady Directional Solidification