Abstract:Normally, the microstructure of eutectic and hypereutectic Al-Si alloys consists of Al-Si eutectic or Al-Si eutectic + Si I , that is why they have good wear-resistance properties, but their ductility decreases somewhat, which can be improved by the appearance of non-equilibrium α-aluminum grains. In present work, a recrystallization and partial melting (RAP) technique was applied in the preliminary research to investigate the solidification behavior of the eutectics at high cooling rate. The results show that numerous α-Al dendrites appeared instead of the eutectic structure. In the followed researches, the combination of some technological procedures, based on the competitive growth of dendrites and eutectics, such as heterogeneous nucleation and high cooling rate, were applied: A413.0 and A390.0 alloys were melted in resistant furnace and poured into a mold, made of copper at one side and of steel at another, which is connected to the temperature measuring device via four K-class thermocouples. The various pouring regimes: gravity, via 45 0 tilt cooling slope and injection with Argon gas for 2 min. before pouring, were applied at different temperatures of 680, 650, 630 0 C. The results show that the hetero-structure of eutectic and hyper-eutectic Al-Si alloys, consists of non-equilibrium α-Al grains, primary silicon and eutectics was obtained. Grain size varies with cooling rate, with minimum value of 10 μm when the specimen thickness is 5 mm. Non-dendritic grains were achieved with semi-solid treatment (pouring via cooling slope). The elongation of alloy is expected to be enhanced due to the appearance of α-Al grains.

Forming Mechanism of α-Phase in Directionally Solidified Microstructure of Hypereutectic Cu-Cr Alloy

Formation of Heterostructure with Appearance of α-Al Phase in Hyper- and Eutectic Al-Si Alloys by Solidification at High Rate

Directional Solidification of Cu-Cr Alloy

Microstructure Evolution and Growth Behaviors of Faceted Phase in Directionally Solidified Al-Yalloys I. Microstructure Evolution of Directionally Solidified Al-15%Y Hypereutectic Alloy

The microstructure of a directionalloy solidified NiAl-Cr(Mo)-Hf alloy

The characterization of Fe-rich phases in a high-pressure die cast hypoeutectic aluminum-silicon alloy

Phase Separation of AlCoCrFeNi2.1 Eutectic High-Entropy Alloy During Directional Solidification and Their Effect on Tensile Properties

Phase and microstructure evolution in Cu-In-Cr alloys

Analysis on Microstructure of Al-40%Cu Alloy in Directional Solidification Process

Microstructure and Solidification Mode of AlTiFeNiCuCr_x High-entropy Alloy with Multi-Principal Elements

Microstructural evolution and phase selection during solidification of AlCrCuFeNi high entropy alloy

Formation of a Two-Phase Microstructure in Fe–Cr–Ni Alloy During Directional Solidification

Microstructure Evolution of Directionally Solidified Al-12%Ni Hypereutectic Alloy

Influence of Ti on Solid Microstructure and Phase Transformation of Cu75Cr25 Alloy at Different Cooling Conditions

Mechanical Alloying of the Immiscible Cu-60wt%Cr Alloy: Phase Transitions, Microstructure, and Thermodynamic Characteristics

Microstructure Evolution and Mechanical Property of Directionally Solidified CoCrFeMnNi High Entropy Alloy

Microstructure and Phase Stability Studies on Heusler Phase Ni2AlHf and G-phase Ni16Hf6Si7in Directionally Solidified NiAl–Cr(Mo) Eutectic Alloyed with Hf

Microstructure and Nanomechanical Behavior of Individual Phase in Β-Solidifying Ti-43Al-5Nb-3.5Cr-1Zr Alloy

Phase Transformation Behavior of a Β-Solidifying Γ-Tial-based Alloy from Different Phase Regions with Various Cooling Methods

Spinodal Decomposition of B2‐phase and Formation of Cr‐Rich Nano‐precipitates in AlCoCrFeNi2.1 Eutectic High‐Entropy Alloy

Microstructure evolution, Cu segregation and tensile properties of CoCrFeNiCu high entropy alloy during directional solidification