Abstract:An equiatomic CoCrFeMnNi high-entropy alloy, which crystallizes in the face-centered cubic (fcc) crystal structure, was produced by arc melting and drop casting. The drop-cast ingots were homogenized, cold rolled and recrystallized to obtain single-phase microstructures with three different grain sizes in the range 4–160μm. Quasi-static tensile tests at an engineering strain rate of 10−3s−1 were then performed at temperatures between 77 and 1073K. Yield strength, ultimate tensile strength and elongation to fracture all increased with decreasing temperature. During the initial stages of plasticity (up to ∼2% strain), deformation occurs by planar dislocation glide on the normal fcc slip system, {111}〈110〉, at all the temperatures and grain sizes investigated. Undissociated 1/2〈110〉 dislocations were observed, as were numerous stacking faults, which imply the dissociation of several of these dislocations into 1/6〈112〉 Shockley partials. At later stages (∼20% strain), nanoscale deformation twins were observed after interrupted tests at 77K, but not in specimens tested at room temperature, where plasticity occurred exclusively by the aforementioned dislocations which organized into cells. Deformation twinning, by continually introducing new interfaces and decreasing the mean free path of dislocations during tensile testing (“dynamic Hall–Petch”), produces a high degree of work hardening and a significant increase in the ultimate tensile strength. This increased work hardening prevents the early onset of necking instability and is a reason for the enhanced ductility observed at 77K. A second reason is that twinning can provide an additional deformation mode to accommodate plasticity. However, twinning cannot explain the increase in yield strength with decreasing temperature in our high-entropy alloy since it was not observed in the early stages of plastic deformation. Since strong temperature dependencies of yield strength are also seen in binary fcc solid solution alloys, it may be an inherent solute effect, which needs further study.

Microstructure evolution, Cu segregation and tensile properties of CoCrFeNiCu high entropy alloy during directional solidification

Effect of Co Addition on Solidification Velocity, Hardness and Refined Structure Transformation Mechanisms of Undercooled Ni-Cu-Co Alloys

Rapid Solidification Structure Refinement Mechanism in Highly Undercooled Cu Based Ternary Alloys

Microstructure evolution and strengthening mechanism of directional solidification Ni40.5Co30Cr11Fe11Al6Ta1.5 high entropy alloy

Microstructure Evolution and Compressive Property Variation of Al CoCrFeNi High Entropy Alloys Produced by Directional Solidification

Microstructure Evolution and Tensile Property of a CuMnFeCoNi High-Entropy Alloy During Thermomechanical Treatment

The influences of temperature and microstructure on the tensile properties of a CoCrFeMnNi high-entropy alloy

Strength and ductility dual-enhancement of Ni36Co30Fe11Cr11Al6Ti5Nb1 high entropy alloy by directional solidification

Impact of Cu Content on Microstructural Evolution and Mechanical Behavior of CoCrMo0.5TiVCux High-Entropy Alloys

Semi-solid thixotropic behavior and microstructure evolution of cold deformed CoCrCu 1.2 FeNi high-entropy alloy

Investigation of Microstructure Evolution and Phase Selection of Peritectic Cuce Alloy During High-Temperature Gradient Directional Solidification

Microstructure evolution and mechanical properties of CoCrFeNiAl0.3 high entropy alloy produced by ball milling in combination with thermomechanical consolidation

Formation of dendrites and strengthening mechanism of dual-phase Ni36Co30Fe11Cr11Al6Ti6 HEA by directional solidification

Effect of Solidification Segregation on Microstructure and Mechanical Properties of a Ni-Cr-Mo-V Steel Weld Metal

Microstructure Evolution and Compressive Property Variation of CoCrFeNiAlx High Entropy Alloys Produced by Directional Solidification

Copper effects on the microstructures and deformation mechanisms of CoCrFeNi high entropy alloys

Strengthening mechanism of CrCoNi medium-entropy alloy from the partially recrystallized structure to the fully recrystallized heterogeneous structure

Effects of Cu on the high-entropy alloys of Cu x CoCrFeNi: Experiment and molecular dynamics simulations

Crack growth and fracture mechanics of CuCrFeNiCo high-entropy alloy during tension testing

Investigation on solidification structure evolution of deeply undercooled single-phase Ni-Cu-Co alloys

Sintering mechanism and microstructure evolution of a CoCrFeNiMn high entropy alloy fabricated by metal injection molding