Abstract:WC/Fe matrix composites with mass fractions of 30–50 wt% were prepared by gravity casting and infiltration, and the phase composition, microstructure, friction and wear properties of the composites were studied. In addition, the mechanism of the effect of the change of WC mass fraction on the structural evolution and wear properties of the composites was particularly investigated. The results show that the composites are mainly composed of WC, α-Fe, W 2 C, Fe 6 W 6 C, and M 7 C 3 phases. With the increase of WC mass fraction, the microstructure of the composite shows different results, WC particles start to dissolve under the action of high temperature melt, W elements solidly dissolve into the matrix and precipitate into fishbone structure carbide. As the content of WC particles in the prefabricated body increases, the C atoms around the WC particles react with the dissolved W atoms, and due to the cooling of the metal liquid, the energy transferred between the WC and the metal liquid does not make it melt completely before solidification occurs, and the metallurgical reaction between the WC particles and the substrate occurs and produces a dense interface. The WC/Fe matrix composites showed a trend of increasing and then decreasing with the increase of WC content and friction coefficients of 0.36, 0.52, and 0.26. The wear rates were 1.52(mm 3 /N-m) × 10 −5 , 1.24(mm 3 /N-m) × 10 −5 , and 1.57(mm 3 /N-m) × 10 −5 , which showed the opposite trend with the friction coefficients, and the wear rates were compared with the morphology. When the composite was added with 40% WC, the wear rate increased by 27% compared with other parameters. It shows that it has good wear resistance.

Investigation on Microstructure and Fracture of WC Particles Reinforced Steel Matrix Composites by Electroslag Melting and Casting

Dissolution Behavior of WC Particle in WC Steel Matrix Composites by Electroslag Melting and Casting Method

Study on Fracture Toughness of Electro-Slag Melting and Casting WC Steel-Bonded Carbide

Evolution of Reinforcing Phase and Microstructure in WC Particle Reinforced Steel Matrix Composites

Microstructure and mechanical properties of WC reinforced 18Ni300 composites produced by selective laser melting

The Particle Shape Of Wc Governing The Fracture Mechanism Of Particle Reinforced Iron Matrix Composites

Microstructure Evolution of WC/steel Composite by Laser Surface Re-Melting

Interfacial Characteristics of WC Particles Reinforced Hadfield Steel Matrix Composites

Study on WC Particles Reinforced Steel Matrix Revolving Parts Prepared by Centrifugal Casting

Preparation of Warm Compacted and Sintered WC/Carbon Steel Composite and Its Wear-Resistance

A Study on a Cast Steel Reinforced with WC-Metal Matrix Composite

Study of Microstructure of Coarse-grain Tungsten Carbide Composite Produced by In-Situ Metallurgy Reaction

Microstructural and Mechanical Properties of in Situ WC-Fe/Fe Composites

Microstructure Evolution and In-Situ-formed Mechanism of Dual-Scale WC-Fe Reinforced Iron Matrix Composites

Microstructure and Mechanical Properties of Nanocrystalline Wc-Particle-Reinforced Ti-Based Composites with Nano/Ultrafine-Grained Intermetallic Matrix from Spark Plasma Sintering and Crystallization of Amorphous Phase

Fracture Toughness of Tungsten Carbide Reinforced Fe-Matrix Surface Composites

Effect of WC mass fraction on the microstructure and frictional wear properties of WC/Fe matrix composites

Wear Behavior of WC/GCr15 Steel Composite Prepared by Electroslag Melting and Casting

Microstructure and properties of W Cu composites reinforced by in-situ generated WC

Solid Particle Erosion of WC Particles Reinforced Steel matrix Composites

Microstructural evolution and performance analysis of WC-11Co reinforced iron matrix composites