Low Temperature Ageing in Water Vapor and Mechanical Properties of Zta Ceramics

RS Guo,DL Guo,D Zhao,ZF Yang,YR Chen
DOI: https://doi.org/10.1016/s0167-577x(02)00666-3
IF: 3
2002-01-01
Materials Letters
Abstract:ZTA ceramics were conventionally prepared by mixing Al2O3, Y–TZP and sintering aids in water for 2 h, isostatically pressing at 200 MPa and sintering at 1450 °C for 2 h in air. The Y2O3 content in Y–TZP was specially designed to be a little high (3 mol%) to obtain good stability of t-ZrO2. The fraction of t-ZrO2 up to 93% was retained at room temperature after sintering. The ZTA ceramics were then aged in water vapor at 240 °C for different times to adjust the stability of t-ZrO2 and furthermore to optimize the zirconia transformation toughening. It was shown that the fraction of t-ZrO2 gradually decreased to 85% after ageing for 2000 h. In contrast, fracture toughness grew continuously to 7.2 MPa m1/2. Strength went up to the maximum 680 MPa when aged for short times, and then dropped gradually to 620 MPa, which was still higher than that without ageing. These results showed that this ZTA material is a good candidate for applications in humid environments and at elevated temperatures.
What problem does this paper attempt to address?