Preparation and Research of Organic-inorganic Hydrophobic SiO2 Composite Films

Gang XU,Ling-hang WANG,Wei-xing CHEN
DOI: https://doi.org/10.3969/j.issn.1673-9965.2007.03.014
2007-01-01
Abstract:Hydrophobic non-fluorine SiO2 coextruded film was prepared from Si(OC2H5)4 and CnH2n+1Si(OCH3)3(n=7~12) instead of Fluoro-organosilane using Sol-Gel method.The character of colloid was inferred from thermogravimetric analysis(TG) and differential thermal analysis(DTA).IR transmittance of films heat-treated at different temperature was examined.The surface of film was characterized by SEM.Anticorrosion and cohesion properties were also discussed here.The results indicate that the heat treatment temperature of the composite thin film should be lower than 300 ℃ to avoid the burning of-CH3.After heat treatment,the content of SiO2 of film increases.The average contact angle of thin films increases with the increment of coating times,and the max value is 110.2°.The films have better hydrophobicity,anticorrosion and cohesion,which amount to the best grade according to GB1720-88.
What problem does this paper attempt to address?