Abstract:High-hardness hydrophobic anti-reflection thin films were prepared by a mixture of acid-catalyzed and alkali-catalyzed sols using tetraethyl silicate (TEOS) and methyltriethoxysilane (MTES) bisilicon sources as precursors. The alkali-catalyzed SiO 2 sol and the acid-catalyzed SiO 2 sol modified with aliphatic alcohol ethoxylated ether (AEO) were synthesized firstly, and then the acid-catalyzed SiO 2 sol was doped into the alkali-catalyzed SiO 2 sol in a certain ratio to prepare the anti-reflection thin films. The effects of the doping ratio of acid-catalyzed SiO 2 sol on the microstructures and properties of thin films were investigated. The experimental results show that both the transmittance and the contact angle increase and then decrease with the increasing of the doping ratio of acid-catalyzed SiO 2 sol, and the surface hardness and adhesion are gradually enhanced. When the doping ratio of acid-catalyzed SiO 2 sol is 30%, the average transmittance of the reflectance-reducing film is 92.51% in the wavelength range of 400–1100 nm, which is 5.17% higher than that of the blank glass. The water contact angle of the reflectance-reducing film is up to 92°, and the adhesion of the film is the highest level 0. After 100 h of UV exposure, the transmittance of the film was reduced by 1.1%.

Preparation and Properties of Methyl-Situ-modified Sol-Gel Hydrophobic Anti-Reflective SiO2 Coating

Sol-gel Preparation of a Silica Antireflective Coating with Enhanced Hydrophobicity and Optical Stability in Vacuum

Preparation and Research of Hydrophobic PDMS/Nano-SiO2 Modified SiO2 Coating

Preparation of Durable Hydrophobic and Antireflective Silica Coating

Preparation of Octyltrimethoxysilane Modified SiO$lt;inf$gt;2$lt;/inf$gt; Hydrophobic Antireflective Coating

Hydrophobic and Optical Properties of Silica Antireflective Coating Prepared Via Sol-Gel Method

Hydrophobic and Optical Properties of HMDS/Silica Hybrid Antireflective Coating Prepared via Sol-gel Method

Comparative Study on Hydrophobic Anti-Reflective Coatings from Methyl-Modified Silica Sols and Vapour-Phase Silylation

Preparation of Organically Modified Silica Sols and Hydrophobic Films

Study of the Preparation and Properties of Nano-structure Hydrophobic and Anti-reflective Silica Films

SURFACE MODIFICATION AND CONTAMINATION RESISTANCE OF SOL-GEL SiO2 DERIVED ANTIREFLECTIVE COATINGS

Preparation of Hydrophobic Optical Silica Thin Film with Sol-gel Method

Preparation and properties of hydrophobic organic-inorganic silica hybrid films

Preparation and Properties of Superhydrophobic Fluoroalkylsilane Coatings

HYDROPHOBIC BEHAVIOR OF NANOPOROUS SILICA FILMS WITH LOW REFRACTIVE INDEX

Sol-Gel Preparation of HTMS-Silica Hydrophobic Coatings with High Environment-Resistance

Preparation of high hardness hydrophobic SiO2 anti reflective thin films from mixed acid catalyzed and alkali catalyzed sols

Sol-gel Preparation of Hydrophobic Silica Antireflective Coatings with Low Refractive Index by Base/acid Two-Step Catalysis.

Preparation of Hydrophobic Coatings with Methyltrimethoxysilane Modified Si-sol

Sol-gel Preparation of Hydrophobic Silica Coating-materials with Ultralow Refractive Index

Properties of Coating Film Based on Silsesquioxanes Derived from (Γ-Methacryloxypropyl) Trimethoxysilanes