Abstract:Large-scale beta-tricalcium phosphate (beta-TCP) hexagonal single crystals were synthesized at a relatively low temperature (150 degrees C) by using a solution-phase method. The solvent, ethylene glycol, played an important role during the formation of the homogeneous submicron-sized crystals. Unlike the conventional understanding of a single crystal, the wall of the formed beta-TCP hexagonal was well crystallized, showing different physicochemical properties from the bulk part. The dissolution spots were anisotropically distributed throughout the single crystal. The bulk part dissolved readily from the top and bottom planes in the undersaturated solutions, but the thin hexagonal wall could be stable against any dissolution even in pure water. These differences between the wall and the bulk part were attributed to the different crystallinities and defect densities in their structures. It was suggested that the low defect number might stem from the solvent-interface exchange that was allowed the edge surfaces in contact with the solution. And the rapid growth of the particles resulted in the randomly distributed defects in the bulk part, which induced a selective dissolution along the c-axis of beta-TCP. Furthermore, the stability of wall could be explained by a size effect during the nanodemineralization. It was interesting that both the wall and the bulk part shared the exact same lattice fringes under the transmission electron microscope. This phenomenon implied that both components were crystallographically identical so that they were constructed into an integral single crystal of beta-TCP. The distinct dissolution behaviors of these, two parts in one single crystal resulted in the formation of porous, gearlike, and ringlike single crystals at different demineralization stages, which demonstrated an easy control of crystal morphology patterns by using the anisotropic dissolution behavior.

Rapid Wet Synthesis Of Nano-Sized Beta-Tcp By Using Dialysis

Dialysis Efficiency In Rapid Synthesis Of Nano-Hydroxyapatite

A Low Temperature Co-Precipitation Preparation of Nano-Sized Zinc Containing Β-Tricalcium Phosphate Powders

Preparation of highly purified β-tricalcium phosphate ceramics with a microdispersion process

Microwave-assisted Rapid Synthesis of Hexagonal Α-Zirconium Phosphate Nanodisks As a Pickering Emulsion Stabilizer

Solvothermal Synthesis of Β-Tricalcium Phosphate Porous Nanospheres by Using Organic Phosphorus Source and Their Biomedical Potentials

Preparation of Nanosized Β-Tricalcium Phosphate Particles with Zn Substitution

Preparation And Characterisation Of Nano-Sized Beta-Tricalcium Phosphate With A Ps Template Method

Synthesis, Sintering Behavior and Morphology of Β-Tricalcium Phosphate Via Sol-Gel Self-Propagating Combustion Technique

A Systematic Study of the Effect of pH on the Initialization of Ca-deficient Hydroxyapatite to β-TCP Nanoparticles

Structural Components and Anisotropic Dissolution Behaviors in One Hexagonal Single Crystal of Β-Tricalcium Phosphate

Dissolution Behavior of Submicron Biphasic Tricalcium Phosphate Powders

Microemulsion Synthesis of Mesoporous β-tricalcium Phosphate Powder with a Novel System

α-Calcium Sulfate Hemihydrate Nanorods Synthesis: A Method for Nanoparticle Preparation by Mesocrystallization

Low Temperature Preparation of Α-Tricalcium Phosphate Up-Converted Luminescence Nano Phosphor

Ba 4 Ti 13 O 30 Nanocrystals Prepared by Hydrothermal Method

Influence of Solvent Polarity on Synthesis of Beta - Tricalcium Phosphate

Preparation of nano-sized strontium containing tricalcium phosphate particles

Phase-Tunable Calcium Phosphate Biomaterials Synthesis and Application in Protein Delivery

Properties of Β-Ca3(po4)2 Bioceramics Prepared Using Nano-Size Powders

Dialysis Preparation of Zinc-Substituted Nano-Hydroxyapatite and Its Characterization