Abstract:A type of novel copper-based catalysts supported on MIL-125(Ti), a kind of metal–organic frameworks (MOFs), noted as Cu-MIL-125(Ti), was synthesized for the selective catalytic reduction (SCR) of NO with CO. The reactivity of Cu-MIL-125 catalysts for selective catalytic reduction of NO by CO (SCR-CO) was evaluated in a fixed bed reactor. A number of characterization techniques were used to explore the basic physical–chemical properties and the reaction mechanism. The results showed that the large specific surface area and micro-mesopores of the MIL-125 carrier promoted the high dispersion of Cu species, leading to the outstanding SCR-CO performance. Among the results, 90 % NO conversion and 92 % N 2 selectivity were proved for the 6.2Cu-MIL-125 catalyst at 325 °C in oxygen-rich environment. XRD results showed that the metal organic frame structure and TiO 2 structure coexisted in the catalysts, which was the major factor to influence the NO reduction efficiency. XPS characterization and H 2 -TPR reduction results showed that the catalytic performance of the catalyst was mainly determined by the path of Cu 2+ reduction to Cu + and then Cu + to Cu 0 . Lewis acid on the catalyst surface played an important role in the CO-SCR reaction. In situ DRIFTS study proved that NO was first adsorbed on the surface of the catalyst to form different nitrate, NCO and isocyanate species. Then the adsorbed NO and the intermediates reacted with gaseous CO, which is a typical interaction between adsorbed molecules and gas molecules. Oxygen vacancies on the catalyst surface was involved in the reaction of CO to CO 2 . The whole reaction follows the M–K mechanism and the E-R mechanism. A preliminary reaction pathway was proposed based on the in situ DRIFTS results.

A Novel Catalyst for NO Reduction by CO

Effect of Water on the Performance of Silica-Pillared Layered Niobate-Supported Copper Oxide Catalyst for NO Reduction by CO

Preparation, Characterization and Activity of Novel Silica-Pillared Layered Titanoniobate Supported Copper Catalysts for the Direct Decomposition of NO

Investigation of Fe-Ni Mixed-Oxide Catalysts for the Reduction of NO by CO: Physicochemical Properties and Catalytic Performance

Co Single Atoms and CoOx Nanoclusters Anchored on Ce0.75Zr0.25O2 Synergistically Boosts the NO Reduction by CO

Nickel foam supported CuCe mixed metal oxide as monolith catalyst for NO removal

The Effect of SiO2 on a Novel CeO2–WO3/TiO2 Catalyst for the Selective Catalytic Reduction of NO with NH3

New Silica-Pillared Layered Titanoniobate Supported Cu Catalysts for the Direct Decomposition of NO

Flower-like CuO/CeO2-NiO Microspheres Catalysts for the NO Reduction by CO: Significant Promoting Effect of Nickel

Nanosheets-assembled Ni (co) Doped CeO2 Microspheres Toward NO + CO Reaction

Hollow Mn-doped CeO2@Co3O4 catalyst for NO reduction by CO

Modification of MnCo₂Oₓ Catalysts by NbOₓ for Low Temperature Selective Catalytic Reduction of NO with NH₃

Spinel Structured CoaMnbOx Mixed Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH3

Mn‐Fe‐Ce Coating Onto Cordierite Monoliths As Structured Catalysts for NO Catalytic Oxidation

Peanut-Shaped Cu–Mn Nano-Hollow Spinel with Oxygen Vacancies as Catalysts for Low-Temperature NO Reduction by CO

CuO/Sn_(0.8)Ti_(0.2)O_2 Catalyst: Characterization and Catalytic Performance in NO+CO Reaction

Copper-based catalysts supported on novel Metal-Organic Framework MIL-125(Ti) for selective catalytic reduction of NO with CO

Hierarchically interconnected porous Mn Co3-O4 spinels for Low-temperature catalytic reduction of NO by CO

Single Ir Atoms Anchored on Ordered Mesoporous WO 3 Are Highly Efficient for the Selective Catalytic Reduction of NO with CO under Oxygen‐rich Conditions

Unravelling the structure sensitivity of CuO/SiO2 catalysts in NO + CO reaction

Study of a catalyst supported on rice husk ash for NO reduction with carbon monoxide