Abstract:Co-based catalysts have been widely applied in NO reduction by CO but still suffer from the unsatisfactory low-temperature catalytic performance. Here, a series of catalysts with a Co3O4–CoO heterointerface were in-situ-prepared and first applied into NO reduction by CO. Compared with single-phase samples, the catalysts with the Co3O4–CoO heterointerface exhibited superior catalytic performance. The best CoOx-350-7 sample showed a lowest apparent active energy (54.2 kJ·mol–1) and achieved 100% NO conversion at 150 °C (gas hourly space velocity = 50 000 h–1). The role of CoO as well as the structure–activity relationship between the interfacial effect and catalytic activity were deeply investigated. Abundant oxygen vacancies were induced due to the introduction of CoO species, and thus, the reducibility and oxygen migration of Co3O4–CoO catalysts were enhanced. The introduction of CoO not only optimized the NO adsorption but also enhanced electron donation ability from the catalyst to adsorbed NO. Moreover, the presence of CoO coupled with oxygen vacancies regulated the CO adsorption/conversion on the catalysts and thus promoted the exposure and reactivation of active sites for the reaction cycles. Accordingly, the stimulated dissociation of NO and the formation of −NCO could enhance the NO conversion to N2 at lower and higher temperatures, respectively.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.1c01593?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.1c01593</a>.Thermal analysis profiles; XRD pattern of CoOx precursor and CoOx-T-3 samples; FT-IR spectra, N2 adsorption–desorption isotherms, BJH pore size distribution curves, texture properties, XPS survey spectra and low-temperature EPR spectra, CO-TPD curves of Co3O4, CoOx-350-t, and CoO samples; N2 yield of Co3O4, CoOx-350-t, and CoO samples; NO conversion of CoOx-450-t catalysts; catalytic stability test of CoOx-350-7 sample; NO conversion under different NO/CO ratios in reaction gas over CoOx-350-7; normalized reaction rates and Arrhenius plots for the rate of NO conversion over Co3O4, CoOx-350-t, and CoO catalysts; in situ DRIFTS spectra for CO adsorption for Co3O4, CoOx-350-7, and CoO catalysts; in situ DRIFTS spectra for NO adsorption and CO + NO coadsorption over CoO catalysts; schematic structure models of Co3O4 {001}, CoO {100}, and Co3O4–CoO heterostructure; PDOS plots of Co3O4 and CoO layers; adsorption energy of NO and Bader charge of NO; PDOS plots of NO on different Co3O4 and CoO layers (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.1c01593/suppl_file/sc1c01593_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Hierarchically interconnected porous Mn Co3-O4 spinels for Low-temperature catalytic reduction of NO by CO

Peanut-Shaped Cu–Mn Nano-Hollow Spinel with Oxygen Vacancies as Catalysts for Low-Temperature NO Reduction by CO

Facile synthesis of Schistose-like Co-Mn oxides for low-temperature catalytic oxidation of NO with enhanced SO 2 /H 2 O tolerance

Rational Design of High-Performance DeNOx Catalysts Based on MnxCo3–xO4 Nanocages Derived from Metal–Organic Frameworks

Design of robust Co-doped Mn3O4 spinel catalysts for selective catalytic reduction of NO with NH3 at low temperatures

Hollow Mn-doped CeO2@Co3O4 catalyst for NO reduction by CO

In situ synthesis of low-valence MnO/Mn 3 O 4 catalyst via carbon-acid hydrothermal strategy for NO removal

Cobalt doped Fe-Mn@CNTs catalysts with highly stability for low-temperature selective catalytic reduction of NOx

Unveiling the Promotion Effects of CoO on Low-Temperature NO Reduction with CO over an In-Situ -Established Co 3 O 4 –CoO Heterostructure

One-step synthesis by redox co-precipitation method for low-dimensional Me-Mn bi-metal oxides (Me=Co, Ni, Sn) as SCR DeNOx catalysts

Synthesis of novel Co(3-x)MnxO4@TiO2 core-shell catalyst for low-temperature NH3-SCR of NOx with enhanced SO2 tolerance

Transition Metal (fe2o3, Co3O4 and NiO)-Promoted CuO-Based Α-Mno2 Nanowire Catalysts for Low-Temperature CO Oxidation

CoO/Co/N-C nanoparticles embedded in carbon as mediate for oxygen reduction electrocatalysts

Insights into the highly activity CuMgFe oxides for the selective catalytic reduction of NO by CO: Structure-activity relationships and K/SO2 poisoning mechanism

Design of meso-TiO2@MnOx-CeOx/CNTs with a core-shell structure as DeNOx catalysts: Promotion of activity, stability and SO2-tolerance

A novel highly active catalyst form CuFeMg layered double oxides for the selective catalytic reduction of NO by CO

Low-temperature and stable CO oxidation of in-situ grown monolithic Mn3O4/TiO2 catalysts

Ternary MnCoVO catalysts with remarkable deNO performance: Dual acid-redox sites control strategy

Designing Efficient Nitrate Reduction Electrocatalysts by Identifying and Optimizing Active Sites of Co-Based Spinels

Effect of reduction on NO + CO reaction performance of CuO-Co3O4 symbiotic oxide porous nanosheet and DFT calculation

Electrocatalytic reduction of nitrate to ammonia on low-cost manganese-incorporated Co3O4 nanotubes