Low-dose O<sup>3+</sup>ion-implanted active optical planar waveguides in Nd : YAG crystals: guiding properties and micro-luminescence characterization

Yan-Xia Kong,Feng Chen,D Jaque,Yang Tan,Ning-Ning Dong,Qing-Ming Lu,Hong-Ji Ma
DOI: https://doi.org/10.1088/0022-3727/41/17/175112
2008-01-01
Abstract:We report, for the first time to our knowledge, on the active optical planar waveguides in Nd : YAG laser crystals fabricated by O3+ ion implantation at low doses of similar to 10(14) ions cm(-2). The reconstructed refractive index profiles based on the measured dark-mode spectroscopy show that an enhanced refractive index well is created in the near-surface region, forming a non-leaky waveguide structure. With thermal annealing treatment at 260 degrees C for 90 min, the propagation losses of the waveguides could be reduced to similar to 3 dB cm(-1) at a wavelength of 632.8 nm. The micro-luminescence investigation reveals that the emission bands of Nd3+ ions are not significantly affected by the waveguide formation processing, which shows promising potentials for efficient waveguide laser operations at near-infrared wavelength bands.
What problem does this paper attempt to address?