Abstract:This study compares the microstructure and tensile properties of Ti6Al4V components fabricated by laser direct metal deposition (LDMD) additive manufacturing (AM) in the transverse and longitudinal directions. The results show anisotropic tensile properties with the transverse direction having high tensile and fracture strengths and the longitudinal direction having a high elongation and reduction of cross section. The anisotropic mechanical properties are attributed to the anisotropic microstructural distribution. The transverse tensile specimen is composed of short columnar prior-β grains which grow perpendicular to the tensile direction, and have a lamellar structure. Along the β grain boundary, αGB and large α colonies were identified. However, the longitudinal specimen shows that the long β structure is parallel to the tensile axis and that the microstructure is composed of basket-woven α phases with shorter α plates and smaller colony sizes compared with those in the transverse specimen. The fracture mechanism induced by the anisotropic microstructure along the transverse and longitudinal directions was compared by examining the fracture process in real-time using uniaxial in-situ scanning electron microscopy (SEM) tensile testing. The results show that shear fracture, which is caused by the vertical β grain boundaries and large α colonies with long α plates, occurs in the transverse specimen. The shear mode is the main reason behind the enhanced tensile strength and fracture strength due to the high resistance to microcrack propagation. However, in the longitudinal specimens, symmetric necking behavior due to the fine α grains resulted in uniform deformation of the grains on both sides of the grain boundaries, inducing greater elongation.

Low Cycle Fatigue Behavior of Laser Melting Deposited TC18 Titanium Alloy

A Study of the Back Stress and the Friction Stress Behaviors of Ti-6Al-4V Alloy During Low Cycle Fatigue at Room Temperature

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

In-Situ Tensile Deformation Behavior Of As-Built Laser Direct Metal Deposited Ti-6al-4v Alloy At 200 Degrees C

Micro-deformation behavior of laser melting deposited multi-gradient TC4/TC11 alloy under tension-tension cyclic loading

In-situ Investigation of the Anisotropic Mechanical Properties of Laser Direct Metal Deposition Ti6Al4V Alloy

Microstructure evolution and cyclic deformation behavior of Ti-6Al-4 V alloy via electron beam melting during low cycle fatigue

In-Situ SEM Study on Deformation and Failure Mechanism of TC4 Titanium Alloy by Laser Additive Manufacturing

Influence of microstructure on strain controlled low cycle fatigue crack initiation and propagation of Ti-55531 alloy

Fatigue cracking behavior and life assessment of TC11 titanium alloy in very high cycle regime at two working temperatures

Microstructure based cracking behavior and life assessment of titanium alloy under very-high-cycle fatigue with elevated temperatures

Investigation of fatigue behavior of laser powder bed fusion Ti-6Al-4V: Roles of heat treatment and microstructure

Life Prediction and Failure Analysis in Laser Powder Bed Fused TiC/Ti6Al4V Titanium Matrix Composite under High Cycle and Very High Cycle Fatigue Conditions

Slip dominated planar anisotropy of low cycle fatigue behavior of commercially pure titanium

Remarkable increase in high-cycle fatigue resistance in a titanium alloy with a fully lamellar microstructure

Low-Cycle Fatigue Behavior and Fracture Characteristics of Low-Cost Ti-2Fe-0.1B Alloy

X-ray imaging of defect population and the effect on high cycle fatigue life of laser additive manufactured Ti6Al4V alloys

Failure Behavior of Laser Metal Deposited Additive Manufacturing Ti-6Al-4V: Effects of Stress State and Initial Defects

Effect of three-stage heat treatment on the composite waveform and variable amplitude fatigue properties of TC4 titanium alloy pulsed laser-arc hybrid welded joints

In Situ Tensile Observation of the Effect of Annealing on Fracture Behavior of Laser Additive Manufactured Titanium Alloy

Analysis of Room-Temperature/High-temperature High-Cycle Fatigue Performance of Laser Additive Manufactured Ti65 Titanium Alloy