Abstract:Titanium-clad (TC) bimetallic steel is able to integrate the superior corrosion resistance of titanium alloy into traditional corrosion-susceptible structural steels, producing prominent life-cycle safety, serviceability and durability. Nevertheless, the relevant seismic performance and fatigue behaviour reported in existing literature are still limited and insufficient to support the codification for structural design of such advanced steel. In order to develop proper plastic/seismic design methodology for TC bimetallic steel structure, the cyclic behaviours and low-cycle fatigue life prediction of such metal must be thoroughly investigated. This paper aims to study the lowcycle fatigue behaviour of hot-rolled bonded TC bimetallic steel manufactured from TA2 titanium alloy and Q355B structural steel. The strain amplitude of low-cycle fatigue (LCF) test ranges from 0.5% to 2.5%, and the strain ratio applied herein includes 0 and -1. The experimental phenomenon, LCF failure mechanism, cyclic stress-strain relationship of different tests are thoroughly compared and discussed. Besides, the influence of strain rate and bond strength are simultaneously demonstrated. The LCF life are fitted and validated through BasquinCoffin-Manson model, Kuroda model and energy method, respectively. The research outcomes demonstrate that the LCF cracks of TC bimetallic steel tend to be initiated at the cladding layer and propagated into the substrate layer due to a coupled buckling-fatigue failure mechanism. Several representative fatigue behaviour of conventional mild (CM) steels including the three-stage cyclic softening and mean stress relaxation have not been observed in this experimental study. The strain rate exhibits distinct influence on the LCF life and failure mechanism. Both Basquin-Coffin-Manson model and energy method can provide more favourable prediction accuracy for LCF life of TC bimetallic steel than the Kuroda model. Generally the LCF life of TC bimetallic steel is shorter than that of structural steels, stainless steels, titanium alloys and stainless-clad (SC) bimetallic steels. The test records and fatigue-life model parameters obtained can lay a solid foundation for seismic analysis and damage evaluation of TC bimetallic steel structure.

Slip dominated planar anisotropy of low cycle fatigue behavior of commercially pure titanium

A Study of the Back Stress and the Friction Stress Behaviors of Ti-6Al-4V Alloy During Low Cycle Fatigue at Room Temperature

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Revealing interface-assisted plastic anisotropy <i>via in situ</i> transmission electron microscopy tension of lamellar TiAl

Influence of microstructure on strain controlled low cycle fatigue crack initiation and propagation of Ti-55531 alloy

In-plane biaxial low-cycle dwell fatigue behavior of CP-Ti based on DIC method

In‐plane biaxial ratcheting effect and low‐cycle fatigue behavior of CP‐Ti based on DIC method

The Action Mechanism of Rolling Texture on the Anisotropic Behavior of a Pure Titanium Plate

Comparison of multiaxial low cycle fatigue behavior of CP-Ti under strain-controlled mode at different multiaxial strain ratios

Remarkable increase in high-cycle fatigue resistance in a titanium alloy with a fully lamellar microstructure

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Crack nucleation and dislocation activities in titanium alloys with the strong transverse texture: insights for enhancing dwell fatigue resistance

On high‐cycle fatigue anisotropy of an aluminum alloy super‐thick plate

Phase Interface-Induced Dwell Fatigue Cracks in Titanium Alloy with Lamellar Microstructure

Impact of plastic strain amplitude on the cyclic behavior of commercially pure titanium grade 2

Dwell and Normal Cyclic Fatigue Behaviours of Ti60 Alloy

High cycle and very high cycle fatigue of TC17 titanium alloy: Stress ratio effect and fatigue strength modeling

Low cycle fatigue behavior of CP-Ti under multiaxial load-controlled mode at different multiaxial stress ratios

Low-cycle Fatigue Behaviour of Hot-Rolled Titanium-Clad Bimetallic Steel

Effect of grain structure and precipitate on tensile properties and low-cycle fatigue behaviors of 2A55 Al-Cu-Li alloy

Prediction of anisotropic LCF behavior for SLM Ti-6Al-4V considering the spatial orientation of defects