Abstract:The fatigue performance of titanium (Ti) alloys fabricated by laser powder bed fusion (LPBF) is a crucial factor influencing the structural safety in service. The high-cycle fatigue (HCF) of LPBF Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy at the room temperature and 500 degrees C was tested. Compared with the room-temperature samples, the fatigue strength of fatigue samples tested at 500 degrees C is reduced by about 55.8 % after 106 fatigue cycles. Crack initiation on the surface is mainly related to fatigue after fewer cycles under high stress, while interior cracks initiate after a longer fatigue life under low stress. Electron back scattering diffraction (EBSD) was adopted to characterize the orientations of grains on the crack propagation paths and the activated slip systems. All prismatic oriented grains were found to activate prismatic slip systems, the activation of which achieves symmetric slips surrounding crack tips, forms ductile striations, and increases energy absorption during crack propagation. These characteristics are conducive to improved fatigue performance. About half of the basal oriented grains activate prismatic slip systems. These activated prismatic slip systems not only have a high Schmid factor (SF) but also need to have a high geometrical compatibility factor with slip systems activated by adjacent grains. The residual (3 phase and alpha phase are aligned according to the Burgers orientation relationship (BOR), so the (3 phase does not alter the direction of crack propagation. The results were used to predict the fatigue crack propagation paths in LPBF Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy during loading along building and transverse directions were predicted. This, to some extent, provides a basis for comparing fatigue performance of LPBF Ti alloys in different directions.

Analysis of Room-Temperature/High-temperature High-Cycle Fatigue Performance of Laser Additive Manufactured Ti65 Titanium Alloy

High-Temperature Mechanical Performance of Laser Additive Manufactured Ti6242s Alloy

Anisotropic Tensile and Fatigue Properties of Laser Powder Bed Fusion Ti6Al4V under High Temperature

Investigation of fatigue behavior of laser powder bed fusion Ti-6Al-4V: Roles of heat treatment and microstructure

Microstructure Transformed by Heat Treatment to Improve Fatigue Property of Laser Solid Formed Ti6Al4V Titanium Alloy

Regain the Fatigue Strength of Laser Additive Manufactured Ti Alloy Via Laser Shock Peening

Microstructural Features of Ti-6Al-4V Manufactured Via High Power Laser Directed Energy Deposition under Low-Cycle Fatigue

Anisotropic High Cycle Fatigue Property Estimation for Laser Additive Manufactured Ti6Al4V Alloy Dependence on Tomographic Imaging of Defect Population

Influence of Laser Cutting on TC4 Titanium Alloy Sheet

Tailoring microstructure with special bimodal structure to improve the ductility and fatigue life of laser powder bed fused Ti6Al4V alloy

High-Temperature Fracture Behavior of an Α/β Titanium Alloy Manufactured Using Laser Powder Bed Fusion

Very high cycle fatigue behavior of laser powder bed fusion additively manufactured Ti6Al4V alloy at elevated temperature

High cycle fatigue behavior of additively manufactured Ti-6Al-4V alloy with HIP treatment at elevated temperatures

Microstructure and mechanical properties of laser-deposited Ti65 near-alpha titanium alloy

Influences of Grain Orientation on High-Cycle Fatigue Performance of Laser Powder Bed Fused Ti-6.5Al-3.5Mo-1.5Zr-0.3Si Alloy at Room Temperature and 500 °C

X-ray imaging of defect population and the effect on high cycle fatigue life of laser additive manufactured Ti6Al4V alloys

Thermal Fatigue Crack Growth Behaviours of Laser Deposited Ti60A Near Α Titanium Alloy

Microstructure and Mechanical Properties of 600℃High Temperature Titanium Alloy Fabricated by Additive Manufacturing

Long Fatigue Crack Growth Behavior of Ti–6Al–4V Produced Via High-Power Laser Directed Energy Deposition

Low Cycle Fatigue Behavior of Laser Melting Deposited TC18 Titanium Alloy

Effects of Ultrasonic Shot Peening on Fatigue Behavior of TA15 Titanium Alloy Fabricated by Laser Melting Deposition