Dy 3+ -Doped Selenide Glasses for 1.3-Μm Optical Fiber Amplifiers

Graduate School of the Chinese Academy of Sciences,Chen Wei,Luo Lan

DOI: https://doi.org/10.1557/jmr.2005.0325

2005-01-01

Abstract:The Ge x Ga 5 Se (95− x ) glasses, where x = 20, 22.5, 25, 27.5, 29.17, 30, 32.5, and 35, all doped with 0.05 mol% Dy 3+ were prepared and studied. Thermal stabilities, optical properties, and 1.3 μm emission properties of the glasses were investigated. Strong fluorescence centered at 1.34 μm with a bandwidth of 92 nm was observed. Three phenomenological intensity parameters were obtained: Ω 2 =12.64 × 10 −20 , Ω 4 =2.94 × 10 −20 , and Ω 6 =1.48 × 10 −20 cm 2 by Judd-Ofelt analysis. A new method estimating lifetime of overlapping energy level was introduced. Lifetimes of 520 μs were measured for the 1.3 μm transition, and the quantum efficiency was 36.8% according to the new method.