Abstract:Two serial Dy3+-doped and Dy3+, Tm3+-codoped (100-x)(0.8GeS(2)center dot 0.2Ga(2)S(3))center dot xCdI(2) (0 <= x <= 20) chalcohalide glasses were prepared and characterized. By analyzing the absorption and emission measurements of the two serial chalcohalide glasses with the Judd-Ofelt analysis, we were able to calculate its Judd-Ofelt strength parameters Omega(t) (t = 2, 4, 6), transition probabilities, exited state lifetimes, branching ratios, and emission cross-sections. In the Dy3+-doped glasses, increase of CdI2 had positive effect up to 1330nm fluorescence and the emission cross section (sigma(emi)) was estimated to be 4.19 x 10(-20) cm(2) for the 0.2wt% Dy3+-doped 64GeS(2)center dot 16Ga(2)S(3)center dot 20CdI(2) glass. In the Dy3+, Tm3+-codoped glasses, increase of CdI2 diminished the amount of ethane-like units [S-3(Ga)Ge-Ge(Ga)S-3], improved the Tm3+: F-3(4) -> Dy3+: H-6(11/2) energy transfer efficiency and intensified the mid-infrared emissions. The emission cross sections (sigma(emi)) of the 2900 and 4300nm fluorescences were estimated to be 1.68 x 10(-20) and 1.20 x 10(-20) cm(2) respectively for the 0.2wt% Dy3+ and 0.5wt% Tm3+ codoped 64GeS(2)center dot 16Ga(2)S(3)center dot 20CdI(2) glass. These novel chalcohalide glasses are promising candidate materials for fiber-amplifiers and mid-infrared laser devices. (C) 2009 Optical Society of America

Near-Infrared Emission Properties And Energy Transfer Of Tm3+-Doped And Tm3+/Dy3+-Codoped Chalcohalide Glasses

The Near- and Mid-Infrared Emission Properties of Tm3+-doped GeGaS–CsI Chalcogenide Glasses

[Energy Transfer and Mid-Infrared Luminescence Properties of Tm3+ /dy3+ Codoped Chalcohalide Glasses].

Broadband near-infrared emission in Er3+-Tm3+ codoped chalcohalide glasses.

Host dependence of spectroscopic properties of Dy3+- Doped and Dy3+, Tm3+-codped Ge-Ga-S-CdI2 chalcohalide glasses

Optical Properties and Local Structure of Dy3+-doped Chalcogenide and Chalcohalide Glasses

Infrared luminescence of Tm3+-doped chalcohalide glasses in GeS2–In2S3–CsBr system

The 1.23 and 1.47 Mu M Emissions from Tm3+ in Chalcogenide Glasses

Near- and mid-infrared emissions of Dy3+ doped and Dy 3+/Tm3+co-doped lead cesium iodide modified chalcohalide glasses

The 1.23 and 1.47μm emissions from Tm3+ in chalcogenide glasses

50gese(2)-25in(2)Se(3)-25csi Glass Doped With Tm3+, Tm3+/Ho3+ And Tm3+/Er3+ For Amplifiers Working At 1.22 Mu M

Tm$^{3+}$-Doped Chalcohalide Glass for Optical Amplifiers at 1.22 and 1.47 $\mu$m

Tm3+-doped chalcohalide glass for optical amplifiers at 1.22 and 1.47 μm

Near infrared emission and energy transfer of bismuth-thulium Co-doped chalcohalide glasses

Study On 1.8 Mu M Emission Of Tm3+ Doped Ges2-Ga2s3-Cscl Glasses

Broadband Near-Ir Emission In Tm/Er-Codoped Ges2-In2s3-Based Chalcohalide Glasses

Mutually Enhanced Near Infrared Emission of Dy3+ and Tm3+ Codoped Chalcohalide Glasses

Broadband Near-IR Emission in Tm/Er-Codoped GeS<sub>2</sub>âIn<sub>2</sub>S<sub>3</sub>-Based Chalcohalide Glasses

50GeSe2-25In2Se3-25CsI glass doped with Tm3+, Tm3+/Ho3+ and Tm3+/Er 3+ for amplifiers working at 1.22 μm

Modified Local Environment and Enhanced Near-Infrared Luminescence of Sm3+ in Chalcohalide Glasses

Spectroscopic properties and Judd-Ofelt analysis of Dy3+-doped and Dy3+, Tm3+-codped Ge-In-S chalcogenide glasses