Mid-infrared emissions of Dy 3+ doped Ga-As-S chalcogenide glasses and fibers and their potential for a 4.2 μm fiber laser

Jian Cui,Xusheng Xiao,Yantao Xu,Xiaoxia Cui,Meiling Chen,Junjiang Guo,Min Lu,Bo Peng,Haitao Guo
DOI: https://doi.org/10.1364/OME.8.002089
2018-01-01
Optical Materials Express
Abstract:For developing an ideal efficient and low-threshold medium for fiber lasers operated at 4 mu m wavebands, 0.05 wt.% to 0.5 wt.% Dy3+ ions doped Ga0.8As39.2S60 chalcogenide glasses were investigated and a 4.2 mu m fiber laser was theoretically studied based on the rate and propagation equations. It was shown that the Ga(0.8)AS(39.2)S(60) glass shows a desirable large Dy3+ ion solubility, which has been increased by an order of magnitude compared to As2S3 glass. Dy-rich nanocrystallines were found when the Dy3+ ions' concentration is more than 0.3wt.% (i.e. 3000 ppmw), and the concentration quenching was found based on spectral analysis: however, no rapid decreases in lifetimes were observed. 0.3wt.% Dy3+ doped Ga0.8As39.2S60 glass possesses relatively large laser quality factor sigma(emi) x tau(mea) = 1.70 x 10(-2)(3) cm(2).s and excellent thermal stability (Delta T = 182 degrees C), which can be successfully drawn into fibers indicating good potential for mid-infrared fiber laser. (C) 2018 Optical Society of America under the terms of the OSA Open Access Publishing Agreement
What problem does this paper attempt to address?