Relying on Energy Transfer to Enhance the 2.9 Μm Emission by Co-Doped Tm3+ Ions in Dy:Y2O3 Transparent Ceramics
Yuxin Pan,Hui Lin,Dawei Zhang,Xiaodong Xu,Xufeng Yao
DOI: https://doi.org/10.1016/j.ceramint.2022.08.316
IF: 5.532
2022-01-01
Ceramics International
Abstract:2 at.% Tm, xat.% Dy:Y2O3 (x = 0, 0.1, 0.5 and 1) transparent ceramics were fabricated via vacuum sintering. The microstructural properties of the prepared ceramics were determined using XRD and SEM. The absorption crosssection of 2 at.% Tm, 1 at.% Dy:Y2O3 ceramic was 0.53 x 10(-20) cm(2) with the FWHM of 43.59 nm. The increased cross-section originates from a large overlapping range appearing in the absorption spectrum of the Dy3+:H-6(15/ 2)-> F-6(5/ 2) and Tm3+:H-3(6) -> H-6(4) transitions. The J-O intensity parameters O2, O4 and O6 and the fluorescence characteristics of the pivotal luminescent level of the Dy3+ ions were investigated. Under 793 nm excitation, the emission cross section of the Tm,Dy:Y2O3 ceramic at 3094 nm was 3.63 x 10(-21) cm(2) with the FWHM of 355 nm. The fluorescence lifetimes of Dy3+:H-6(13/ 2) level of 2 at.% Tm, xat.% Dy:Y2O3 (x = 0.1, 0.5 and 1) ceramics were fitted to be 357 mu s, 282 mu s and 149 mu s, respectively. In order to explore the quenching mechanism of Tm3+:F-3(4) level, the fluorescence lifetimes of Tm3+ -> F-3(4) of the 2 at.% Tm, xat.% Dy:Y2O3 ceramics (x = 0, 0.1, 0.5 and 1) were measured to be 4.878 ms, 462 mu s, 104 mu s and 61 mu s, respectively. The possible energy transfer mechanisms between Tm3+ and Dy3+ ions are discussed. The results show that adding Tm3+ ions to Dy:Y2O3 ceramics can effectively enhance the 2.9 mu m MIR through energy transfer.