Efficient Energy Transfer from Inserted Cdte Quantum Dots to Yvo4:Eu3+ Inverse Opals: A Novel Strategy to Improve and Expand Visible Excitation of Rare Earth Ions
Yongsheng Zhu,Shaobo Cui,Xu Chen,Wen Xu,Pingwei Zhou,Yunfeng Wang,Lin Xu,Hongwei Song,Ling Huang,Wei Huang
DOI: https://doi.org/10.1039/c4nr01845a
IF: 6.7
2014-01-01
Nanoscale
Abstract:Rare earth (RE)-based phosphors demonstrate sharp emission lines, long lifetimes and high luminescence quantum yields; thus, they have been employed in various photoelectric devices, such as light-emitting diodes (LEDs) and solar spectral converters. However, their applications are largely confined by their narrow excitation bands and small absorption cross sections of 4f-4f transitions. In this paper, we demonstrate a novel strategy to improve and expand the visible excitation bands of Eu3+ ions through the interface energy transfer (ET) from CdTe quantum dots (QDs) to YVO4:Eu3+ inverse opal photonic crystals (IOPCs). The significant effects observed in the CdTe QDs/YVO4: Eu3+ IOPCs composites were that the excitation of Eu3+ ions was continuously extended from 450 to 590 nm and that the emission intensity of the D-5(0)-7F(J) transitions was enhanced similar to 20-fold, corresponding to the intrinsic F-7(1)-D-5(1) excitation at 538 nm. Furthermore, in the IOPC network, the ET efficiency from the QDs to YVO4:Eu3+ was greatly improved because of the suppression of energy migration among the CdTe QDs, which gave an optimum ET efficiency as high as 47%. Besides, the modulation of photonic stop bands (PSBs) on the radiative transition rates of the QDs and Eu3+ ions was studied, which showed that the decay lifetime constants for Eu3+ ions were independent of PSBs, while those of QDs demonstrated a suppression in the PSBs. Their physical nature was explained theoretically.