Abstract:Three series of porous carbon fibers were prepared by electrochemical oxidation of a synthetic polyacrylonitrile-based fiber to various degrees. The electrooxidized fibers were characterized by N2 adsorption at 77K, CO2 adsorption at 273K, NaOH neutralization and X-ray photoelectron spectroscopy (XPS). In all cases standard BET surface areas calculated from nitrogen adsorption data barely exceeded the geometric area of the fiber itself (ca 1m2g−1). In contrast, surface areas derived by applying the Dubinin–Radushkevich (DR) method to CO2 adsorption data increased fairly linearly from ca 1 to 132m2g−1 with increasing electrooxidation severity. NaOH uptakes were also found to increase linearly as a function of electrooxidation severity. It is thus inferred that: (1) N2 adsorption at 77K is severely hindered because of activated N2 diffusion effects; and (2) by virtue of their thinner dimension and faster diffusion rate at 273K, CO2 molecules manage to probe the entire pore structure of the carbon fibers. Therefore, a new model based on density functional theory (DFT) was applied to CO2 adsorption data at 273K in order to generate true pore size distributions (PSDs) of the fibers tested. The DFT/CO2 method revealed that the PSDs of the electrooxidized fibers are neither Gaussian nor monomodal. Comparison with steam activated synthetic and natural plant (Kenaf) fibers revealed that ultramicroporous fibers possess PSD peaks at ca 0.4, 0.6, 0.8 and 1.1nm. The peak at ca 0.4 was dominant and negligible when the DR/CO2 to BET/N2 surface area ratios were >1 and <1, respectively. It is therefore concluded that pores of ca 0.4nm width are responsible for activated N2 diffusion at 77K.

Porous structure of pan-based activated carbon fibers

Adsorption and Porous Structure of High-Surface Area PAN-ACF

Study of Microstructure of High-Surface-Area Polyacrylonitrile Activated Carbon Fibers.

Carbon Dioxide Adsorption on Carbon Nanofibers with Different Porous Structures

Study on Pan-Based Activated Carbon Fiber Prepared by Different Activation Methods

Microstructures of PAN-ACF modified by catalytic benzene deposition

Effect of Carbonization Temperature on Microstructure of PAN-based Activated Carbon Fibers Prepared by CO2 Activation

Numerical Analysis of the Porous Structure of Activated Carbons Derived from Synthetic Polymers

Preparation of PAN-based Molecular Sieve ACF and Study of Surface Structure by XPS

Insight into Specific Surface Area, Microporosity and N, P Co-Doping of Porous Carbon Materials in the Acetone Adsorption

Structure and Adsorption Properties of Activated Carbon Aerogels

Adsorption Models and Structural Characterization for Activated Carbon Fibers

Porous Structure and Liquid‐phase Adsorption Properties of Activated Carbon Aerogels

Pore Structures and Adsorption Properties of Fluorinated Activated Carbon Fiber

Comparative studies of porous carbon nanofibers by various activation methods

Pore structure and fractal characteristics of activated carbon fibers characterized by using HRTEM

Study on Pan-Based Activated Carbon Fiber Prepared by Koh Activation Method

Preparation of a Novel PAN/cellulose Acetate-Ag Based Activated Carbon Nanofiber and Its Adsorption Performance for Low-Concentration SO 2

Surface area and pore size distribution of microporous carbon fibers prepared by electrochemical oxidation

Porous carbon fibers from low-temperature sodium amide activation for acetone adsorption

Porous Carbon Nanofibers with Heteroatoms Doped by Electrospinning Exhibit Excellent Acetone and Carbon Dioxide Adsorption Performance: The Contributions of Pore Structure and Functional Groups