Abstract:In this paper, changes in the porous structure of carbon material are investigated during chemical activation of apricot pit at different temperatures. The main purpose of the research has been to study the features of the internal micro- and mesostructure of the carbon surface, as well as to find patterns in the size distribution of pores dependent on the carbonization temperature of plant raw materials and subsequent chemical activation. The object of the study is porous carbon material, obtained from dried apricot fruit pits, pre-crushing, and cleaned from the core. This raw material has been carbonized at 300–900 °C with an interval of 100 °C and subjected to chemical activation by potassium hydroxide in the weight ratio XК, where ХК = m(KOH)/m(C). Thereby, a series of samples C3÷C9 has been obtained. The porous structure characteristics (specific surface area and total pore volume) of porous carbon material have been determined based on the analysis of nitrogen adsorption / desorption isotherms. It has been found that these materials have a frame structure with a large number of micropores. The analysis of literature data has revealed that the experimental curves belong to the isotherms that are characteristic of multilayer adsorption in micro- and mesopores of materials of organic origin. The hysteresis loop observed on these isotherms is related to the sorption processes in narrow pores. It has been found that carbonization of raw materials and chemical activation contribute to the cleaning of the frame structure, and there are acceptable modes of heat treatment of raw materials of plant origin, which determine the optimal pore size distribution and have a specific surface area S = (1042–1313) m2/g. With the help of scanning electron microscopy, the peculiarities of the formation of impurities on the surface of the original samples have been studied and their nature has been elucidated. It has been found that the largest total pore area has a sample carbonized at 600 oC, and the largest pore volume Vtotal = 0.68 cm3/g for sample C3 is associated with a significant number of mesopores in the porous structure. As the carbonation temperature increases to 800-900 °C, narrow micropores degenerate and the carbon matrix transforms, resulting in a decrease in both the total pore area and the total porous volume.

Effect of Carbonization Temperature on Microstructure of PAN-based Activated Carbon Fibers Prepared by CO2 Activation

Carbon Dioxide Adsorption on Carbon Nanofibers with Different Porous Structures

Chemical Structure Evolution and Mechanism During Pre-Carbonization of PAN-based Stabilized Fiber in the Temperature Range of 350–600 °C

Effect of amorphous carbon on the tensile behavior of polyacrylonitrile (PAN)-based carbon fibers

Effect of Calcination Temperature and Chemical Composition of PAN-Derived Carbon Microfibers on N2, CO2, and CH4 Adsorption

Effect of beating degree of fiber on the development of porosity in polyacrylonitrile-based activated carbon fiber paper

Effect of oxygen content on the preoxidation structure of polyacrylonitrile fibers

Effect of Temperature on the Adsorption of Organic Vapours on Activated Carbon Fibres

Structure Evolution and Optimization in the Fabrication of Pva-Based Activated Carbon Fibers

A comprehensive study on the effect of carbonization temperature on the physical and chemical properties of carbon fibers

Study on the Changes of Structures and Properties of PAN Fibers during the Cyclic Reaction in Supercritical Carbon Dioxide

Effects of carbonization temperature on structure and mechanical strength of electrospun carbon nanofibrous mats

Properties of Carbon Nanofibers Prepared from Polyacrylonitrile/Poly(methyl Methacrylate) Blend

STUDY ON CARBONIZATION TECHNOLOGY OF LARGE-TOW POLYACRYLONITRIL-BASED PREOXIDIZED FIBER

Hierarchical Pore Structure of Activated Carbon Fabricated by CO2/microwave for Volatile Organic Compounds Adsorption

Adsorption of Volatile Organic Compounds on Activated Carbon Fiber Prepared by Carbon Dioxide

Study on adsorption performance of polyacrylonitrile-based activated carbon fiber for trace of hexavalent chromium

Activated Carbon Powders from Wool Fibers

Influence of carbonization conditions on porous structure of carbon materials

The investigation on microstructure change of activated carbon fiber by oxidation

Evolution mechanism of cyclized structure of PAN-based pre-oxidized fiber during low temperature carbonization process