Abstract:In order to achieve combustion synthesis (CS) of high-density and fine-structured TiC–Al2O3–Al composites, the activation of combustion reactions of 3TiO2–3C–(4+x) Al system with x≥10mol was conducted by means of external electric field. During the field-activated combustion synthesis (FACS), liquid Al in excess stoichiometric amount was generated and it infiltrated into the synthesized TiC–Al2O3 ceramic matrix with porosities, which directly results in a dense TiC–Al2O3–Al composites. The influence of electric field on CS process of the reactive system and the resulting microstructures of TiC–Al2O3–Al composites was investigated. The results show that an external electric field can effectively improve the adiabatic combustion temperature of the reactive system. Therefore a self-sustaining combustion of the system can be induced thermodynamically. In the experiments, both practical combustion temperature and propagation velocity of combustion wave were obviously enhanced with increasing field strength, whereas sizes of the synthesized TiC and Al2O3 particles were significantly decreased at the same time. Under an electric field of 25Vcm−1, TiC–Al2O3–Al composites with a relative density of 92.5% was successfully fabricated through the combustion reaction in the system with x=14mol, in which TiC and Al2O3 particles possess fine-structured sizes of 0.2–1.0μm, with uniform distribution in metal Al.

Effect of an external electric field on the combustion synthesis process of TiO2-C-Al system

Influence of an electric field on combustion synthesis process and microstructures of TiC–Al2O3–Al composites

Microstructure Formation Mechanism of the Combustion Synthesis of TiC-Al_2O_3-Al Composites under Electric Field

Study on the Dense Tic-Al2o3-Al Composites by Electric Field-Activated Combustion Synthesis

Microstructures, Densification and Mechanical Properties of TiC–Al2O3–Al Composite by Field-Activated Combustion Synthesis

Combustion Synthesis of TiC–Fe Composites under the Action of an Electric Field

Combustion Synthesis of Fe-Ti-C System by Electric Field Inducement: Effect of Electric Current on the Synthesis Products

Microstructure evolution of Fe-Ti-C system synthesized by low temperature combustion induced in electric field

Effect of Combustion Temperature on Combustion Synthesis of Ti3AlC2 and Ti2AlC

EFFECTS OF TiAl ADDITION ON COMBUSTION SYNTHESIS OF Ti_2AlC

Effects of different Al contents on combustion synthesis of Ti3AlC2 powders in the Ti-Al-C system

Effects of TiAl3 addition on combustion synthesis of Ti3AlC

Effects of TiAl additions on combustion synthesis of Ti3AlC2 powders

Effects of Tial3 Addition in Ti-Al-C System on Combustion Synthesis of Ti3alc2 Powders

Effects of Tic Addition on Combustion Synthesis of Ti(2)Alc Powders

Preparation and characterization of TiB2-Al2O3 composite powder by combustion synthesis process

Effects of different Ti/C and Al contents on combustion synthesized Ti3AlC2 powders in the Ti-Al-C system

Mechanosynthesis Mechanism of Tic Powders

Effects of carbon contents on combustion synthesis of Ti2AlC powders

Combustion synthesis of ternary carbide Ti3AlC2 in Ti–Al–C system

Effect of Pressure on Combustion Synthesis of TiC/Fe-Cu Composites under the Action of Electric Current