Abstract:A novel composite with in situ synthesized of Ti2(Al,Si)C solid solution reinforced Al matrix was fabricated in Ti2AlC-Al-Si material system via one-step solid solution and densification by spark plasma sintering method. The relationship between microstructure, phase composition and mechanical properties of composites doped with different Si content (1, 2 and 3 wt%) and fabricated at different sintering temperature (580, 570 and 560 °C) were investigated. The optimal sintering temperature of composites with increasing the Si addition was carefully determined. The interface reaction was effectively regulated under different Si additions. X-ray photoelectron spectroscopy (XPS) and nanoindentation test results reveal that Si formed SiC covalent bond in Ti2(Al,Si)C solid solution, and with the increase of Si addition, the hardness and elastic modulus of Ti2(Al,Si)C increased by 6.75% and 4.23% in the composites prepared by the three optimal processes. The tensile tests show that when the addition of Si was 2 wt% and the sintering temperature was 570 °C, the composites demonstrated an optimal balance of strength and plasticity. The ultimate tensile strength reached 226 MPa with a strain of 14.33%. Moreover, when added to 3 wt% and the sintering temperature decreased to 560 °C, the composite achieved a significant improvement in elongation. The performance are mainly attributed to the strengthening of Ti2(Al,Si)C solid solution and the regulation of interface reaction.

Study on the Dense Tic-Al2o3-Al Composites by Electric Field-Activated Combustion Synthesis

Microstructures, Densification and Mechanical Properties of TiC–Al2O3–Al Composite by Field-Activated Combustion Synthesis

Microstructure Formation Mechanism of the Combustion Synthesis of TiC-Al_2O_3-Al Composites under Electric Field

Influence of an electric field on combustion synthesis process and microstructures of TiC–Al2O3–Al composites

Effect of an external electric field on the combustion synthesis process of TiO2-C-Al system

In Situal3ti–al2o3 Intermetallic Matrix Composite: Synthesis, Microstructure, and Compressive Behavior

FLEXURAL STRENGTH OF IN-SITU REACTION PROCESSED Al2O3-Al3Ti-Al COMPOSITES

Microstructure and wear properties of TiC-Al composite fabricated by field activated and low-pressure assisted combustion synthesis

Combustion Synthesis of TiC–Fe Composites under the Action of an Electric Field

Investigation on microstructure and properties of TiC0.5-Al2O3/Cu composites fabricated by a novel in-situ reactive synthesis

Preparation of ti-al based nanophase composite powder by mechanical alloying

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

In Situ Synthesis and Properties of Ti<sub>3</sub>AlC<sub>2</sub>/TiB<sub>2</sub> Composites

Study on synthesis of TiC in Al/TiC composite materials

Microstructure and property of Al/TiC composites prepared by reaction synthesis

Reaction synthesis of Al/TiC composites and the effect of Al content

Study on the Synthesis of Ti3AlC Powder by Combustion

Investigation on the in-situ reaction mechanism of Ti2AlC/TiAl composite prepared by spark plasma sintering

Microstructure characterization and mechanical properties of in situ synthesized Ti2(Al,Si)C reinforced Al composites

In Situ Synthesis of Ti2AlC–Al2O3/TiAl Composite by Vacuum Sintering Mechanically Alloyed TiAl Powder Coated with CNTs

Microstructure evolution of Fe-Ti-C system synthesized by low temperature combustion induced in electric field