Abstract:A supported Ni–P amorphous catalyst (Ni–P/SiO2) was prepared by electroless plating. When the sample was treated at elevated temperatures from 363 to 973 K in N2 flow for 2.0 h, the XRD patterns and SEM morphologies revealed that the Ni–P amorphous alloy crystallized stepwise from 673 to 873 K. The stabilizing effect of the support on the Ni–P amorphous alloy was observed by DSC, TPO, and TPR, which was attributed to the high dispersion of the Ni–P alloy particles in the support matrix, the affinity of SiO2 support for the Ni–P alloy particles, and the transfer of the heat produced during the crystallization from the surface to the bulk of the support. The change in the activity of the as-prepared Ni–P/SiO2 amorphous catalyst during heat treatment was measured using the liquid phase benzaldehyde hydrogenation as a probe and by comparing to that of the corresponding Ni/SiO2 crystalline catalyst. On one hand, the activity of both two catalysts decreased with the increase of the treating temperature owing to the decrease in surface active Ni atoms caused by the coalescence of small Ni particles at high temperature. On the other hand, the two catalysts exhibited considerably different catalytic behaviors during the heating treatment. (1) Only a smooth decrease in the activity of the Ni/SiO2 catalyst was observed with the increase of the treating temperature. While an impressive decrease in the activity of the Ni–P/SiO2 amorphous catalyst was observed in the temperature range from 673 to 873 K corresponding to its crystallization; (2) no significant change in the apparent activation energy (Ea) and the TOF value was observed during the heating pretreatment of the Ni/SiO2 catalyst. However, a considerable increase in Ea and a decrease in the TOF value were observed after the crystallization of the Ni–P/SiO2 amorphous catalyst. These results demonstrated a crystallization deactivation of the Ni–P/SiO2 amorphous catalyst. According to various characterizations, such as EXAFS, XRD, SEM, TEM, XPS, DSC, ICP, TPR, TPO, TPD, and hydrogen chemisorption, the decrease in the number of surface active Ni atoms and the surface P content in the Ni–P alloy, the change in the structural characteristics, and the adsorbing properties of the Ni active sites were the main factors responsible for the deactivation of Ni–P/SiO2 amorphous catalyst during the crystallization.

Amorphous NiP/SiO2 aerogel: Its preparation, its high thermal stability and its activity during the selective hydrogenation of cyclopentadiene to cyclopentene

Sol-Gel Preparation, Characterization and Hydrogenation Property of Silica Supported Ni Catalyst

Selective hydrogenation of cyclopentadiene to cyclopentene over an amorphous NiB/SiO2 catalyst

Hydrogen Production from Partial Oxidation of Propane: Effect of SiC Addition on Ni/Al2O3 Catalyst

Regeneration at Room Temperature for Amorphous Nib/Sio2 Catalyst Deactivated in Cyclopentadiene Hydrogenation

Partial Hydrogenation of Cyclopentadiene over Amorphous NiB Alloy on Α-Alumina and Titania‐modified Α-Alumina

The Crystallization Process and the Hydrogenation Activity of Ni-P/SiO2 Catalyst

High Resistance to Aerial Oxidation of an Amorphous NiB/SiO2 Catalyst: TP‐XRD, TPR and Related Investigations

Amorphous Alloy Deposited on Support and Its Hydrogenation Activity

Crystallization Deactivation of Ni–P/SiO2 Amorphous Catalystand the Stabilizing Effect of Silica Support on the Ni–P Amorphous Structure

Sol–gel preparation of crystalline Ni 12 P 5 /N-doped carbon and amorphous Ni–P–C catalysts and their high catalytic performances toward hydrogenation reduction reaction of 4-nitrophenol

Preparations,Structures and Properties of Amorphous Ni-P Alloy Catalysts

Modification on Ni-P Amorphous Catalyst with Sio2 and Pd

Ultrafine NiO–La2O3–Al2O3 aerogel: a promising catalyst for CH4/CO2 reforming

Preparation and characterization of nickel based catalysts on silica, alumina and titania obtained by sol–gel method

The effect of cyclic oxidation-reduction pretreatments on an amorphous Ni80P20 catalyst: an XPS/UPS/ISS study

Syngas Production Via Combined Oxy-Co2 Reforming of Methane over Gd2O3-modified Ni/SiO2 Catalysts in a Fluidized-Bed Reactor

Nanocatalysts Anchored on Nanofiber Support for High Syngas Production Via Methane Partial Oxidation

Triethanolamine-mediated photodeposition formation of amorphous Ni-P alloy for improved H2-evolution activity of g-C3N4

A highly loaded and dispersed Ni2P/SiO2 catalyst for the hydrotreating reactions

Amorphous Ni-B/γ-Al2O3 catalyst prepared in a modified drying approach and its excellent activity in benzene hydrogenation