Abstract:Nanosilica particles well dispersed in ethanol were modified by 3-(trimethoxysilyl) propyl methacrylate (MPS) and then re-dispersed into methyl methacrylate (MMA) and poly(methyl methacrylate) matrix via a media replacement process and an in situ bulk polymerization process, respectively. The MPS modified status of silica particles and its effects on the dispersion of silica particles in different media and polymer matrix were systematically investigated by FTIR, TG, DLS and TEM. It was found MPS oligomer was the main form for MPS coupling on silica particles surface. Excessive MPS dosage not only resulted in the formation of MPS homo-polymeric particles in media phase, but also the MPS oligomer thick layer on silica surface, which would inevitably induce the small-scale aggregation of silica particles. There existed an appropriate MPS coupling amount for excellent silica dispersity, which is mainly related with the apparent coupling density of MPS molecules on silica particles surface. When the apparent coupling density is 1. 3 similar to 5. 6 mu mol . (m(2) . SiO2)(-1), the MPS coupling efficiency is acceptable and the modification of silica particles is sufficient. Only on this state, silica particles can be dispersed in the monomer and polymer matrix at the primary particles size level, even in the case of 20% silica content. The silica/monomer dispersion prepared via the above processes exhibited high silica dispersity, high silica content, high storage stability and high grafting controllability on silica surface. All of them imply that this kind of dispersion is avail to prepare silica/PMMA composite microspheres via in situ heterogeneous polymerization, and these microspheres would possess controllable morphology and controllable graft interface.

Synthesis of Nanosilver/Pmma Composites Via Ultrasonically Bi-In Situ Emulsion Polymerization

The Preparation And Characterization Of Zns/Pmma Nanocomposites

Synthesis, characterization and reaction kinetics of PMMA/silver nanocomposites prepared via in situ radical polymerization

Preparation of Poly (methyl Methacrylate)/nanometer Calcium Carbonate Composite by In-Situ Emulsion Polymerization

Electrostatic Absorption of Initiator Onto Nanometer SiO2 Particles and In-Situ Emulsion Polymerization of Methyl Methacrylate in the Presence of Modified Nanometer SiO2

Characterization and Synthesis Mechanism of Nanosilver/PAMPS Composites by Microwave

Preparation and characterization of polyacrylamide–silver nanocomposites

Mini-Emulsification and Mini-Emulsion Polymerization of Methyl Methacrylate/Nanosilica Dipsersion

Synthesis and Characterization of PMMA/Al 2 O 3 Composite Particles by in Situ Emulsion Polymerization

Preparation and Characterization of Silica/Pmma Composites with Highly Dispersed Silica Nanoparticles Dispersion of Nanosilica in Mma

Polystyrene-Poly(methyl methacrylate) Silver Nanocomposites: Significant Modification of the Thermal and Electrical Properties by Microwave Irradiation

In Situ Synthesis and Nonlinear Optical Properties of Ag Nanocomposite Polymer Films

Synthesis and characterization of PMMA/Al2O3 composite particles by in situ emulsion polymerization

Preparation of Poly(Methylmethacrylate)/Layered Double Hydroxides Nanocomposites Via in Situ Solution Polymerization

Preparation of Acrylonitrile Polymer/Nanometer Silica Composite Particles by In-Situ Emulsion Polymerization

In-Situ Heterogenous Polymerization of Methyl Methacrylateonto Nanometer Calcium Carbonate Particles

Synthesis and Characterization of Poly(butyl Acrylate-Co-styrene)–silver Nanocomposites by Γ Radiation in W/O Microemulsions

Preparation of a Novel Silver Nanoparticle/Poly(hydroxyethyl Methacrylate) Composite Material

On The Silica/Pmma Nanocomposites

Γ-Radiation Synthesis and Characterization of Polyacrylamide–silver Nanocomposites

Effect of Silver Nanoparticles on the Microstructure, Non-Isothermal Crystallization Behavior and Antibacterial Activity of Polyoxymethylene