Abstract:Nanosilica particles well dispersed in ethanol were modified by 3-(trimethoxysilyl) propyl methacrylate (MPS) and then re-dispersed into methyl methacrylate (MMA) and poly(methyl methacrylate) matrix via a media replacement process and an in situ bulk polymerization process, respectively. The MPS modified status of silica particles and its effects on the dispersion of silica particles in different media and polymer matrix were systematically investigated by FTIR, TG, DLS and TEM. It was found MPS oligomer was the main form for MPS coupling on silica particles surface. Excessive MPS dosage not only resulted in the formation of MPS homo-polymeric particles in media phase, but also the MPS oligomer thick layer on silica surface, which would inevitably induce the small-scale aggregation of silica particles. There existed an appropriate MPS coupling amount for excellent silica dispersity, which is mainly related with the apparent coupling density of MPS molecules on silica particles surface. When the apparent coupling density is 1. 3 similar to 5. 6 mu mol . (m(2) . SiO2)(-1), the MPS coupling efficiency is acceptable and the modification of silica particles is sufficient. Only on this state, silica particles can be dispersed in the monomer and polymer matrix at the primary particles size level, even in the case of 20% silica content. The silica/monomer dispersion prepared via the above processes exhibited high silica dispersity, high silica content, high storage stability and high grafting controllability on silica surface. All of them imply that this kind of dispersion is avail to prepare silica/PMMA composite microspheres via in situ heterogeneous polymerization, and these microspheres would possess controllable morphology and controllable graft interface.

Preparation of Acrylonitrile Polymer/Nanometer Silica Composite Particles by In-Situ Emulsion Polymerization

Influence of Small Amount of Co-Monomers on Acrylonitrile Polymerization in Dimethylformamide (DMF) Solution

Electrostatic Absorption of Initiator Onto Nanometer SiO2 Particles and In-Situ Emulsion Polymerization of Methyl Methacrylate in the Presence of Modified Nanometer SiO2

Poly(L-Lactic Acid)/Sio2 Nanocomposites Via in Situ Melt Polycondensation of L-Lactic Acid in the Presence of Acidic Silica Sol: Preparation and Characterization

Morphology and Formation Mechanism of Poly(butyl Acrylate)/nanosilica Composite Particles Prepared by in Situ Emulsion Polymerization

Anchoring of polyacrylate onto silica and formation of polyacrylate/silica nanocomposite particles via in situ emulsion polymerization

Synthesis and Characterization of Poly(butyl Acrylate)/silica and Poly(butyl Acrylate)/silica/poly(methyl Methacrylate) Composite Particles

Preparation of acrylate polymer/silica nanocomposite particles with high silica encapsulation efficiency via miniemulsion polymerization

Mini-Emulsification and Mini-Emulsion Polymerization of Methyl Methacrylate/Nanosilica Dipsersion

ANCHORING OF AZO INITIATOR AND GRAFTING OF POLY(METHYL METHACRYLATE) ONTO NANAOMETER SILICA

Preparation of Polyacrylonitrile/Nano-SiO2 Composite Particles by Miniemulsion Polymerization

Study on the Activity of Adsorbed Initiator on Nanosilica Particles Surface

Preparation of Mma-Ba-Dmaema Nanosized Latex

Preparation of Poly(methyl Methacrylate)/ultrafine CaCO3 Composite Particles by In-Situ Dispersion Polymerization

Preparation of Poly (methyl Methacrylate)/nanometer Calcium Carbonate Composite by In-Situ Emulsion Polymerization

Investigation of Nano Silica In-Situ Reinforced BA-co-MMA Copolymer

In-Situ Heterogenous Polymerization of Methyl Methacrylateonto Nanometer Calcium Carbonate Particles

Preparation of Mesoporous Carbons from Acrylonitrile-methyl Methacrylate Copolymer/Silica Nanocomposites Synthesized by In-Situ Emulsion Polymerization

Synthesis and Characterization of Self-cross Linking Hybrid Silicone-acrylate Emulsion at Ambient Temperature

Preparation of SiO2/PMMA Composite Particles Via Conventional Emulsion Polymerization

Preparation and Characterization of Silica/Pmma Composites with Highly Dispersed Silica Nanoparticles Dispersion of Nanosilica in Mma