Preparation of Silica Flatting Agent with Large Pore Volume by Using a Micro-sieve Reactor

Wang Chao,Wang Yujun,Luo Guangsheng,Kong Desheng

DOI: https://doi.org/10.3969/j.issn.1008-5548.2012.01.003

2012-01-01

Abstract:The amorphous silica precipitation consisted of primary particles with a diameter of 10 nm was prepared using sodium silicate and sulfuric acid as feedstocks in a micro-sieve reactor.These precipitation was dispersed in ethanol,silica with high fluffy was obtained after spray drying.It was found that because of the high mass transfer rate in this micro-reactor,the supersaturation ratio could reach very high,which was suitable for the formation of tiny primary particles.Fluffy was improved by spray drying,through rapidly evaporating solution of ethanol,porous flatting agent was prepared.When the final pH was equal to 8.5,the specific surface area of silica particles was 251.40 m2/g,pore volume of silica hydrated reached as high as 2.14 mL/g and the average pore size was 34.07 nm.Comparing the amorphous silica with commercial products prepared by fume method,it was found that their properties were close,however,this precipitation method greatly reduced the production cost.