Preparation of Monodisperse Silica Mesoporous Microspheres with Narrow Pore Size Distribution
Jiaqi Shan,Jia Liu,Jiahui Zhu,Lifei Chen,Ting Xu,Xingfa Ren,Xingzhong Guo
DOI: https://doi.org/10.3390/polym16121724
2024-06-17
Abstract:The purpose of this study is to prepare monodisperse silica mesoporous microspheres with narrow pore size distribution to promote their application in the field of liquid chromatography. An improved emulsion method was used to prepare silica mesoporous microspheres, and the rotary evaporation temperature, emulsification speed, dosage of porogen DMF, and dosage of the catalyst NH3·H2O were optimized. Subsequently, these microspheres were respectively treated by alkali-heating, calcination, and sieving. The D50 (particle size at the cumulative particle size distribution percentage of 50%) of as-prepared silica mesoporous microspheres is 26.3 μm, and the D90/D10 (the ratio of particle size at a cumulative particle size distribution percentage of 90% to a cumulative particle size distribution percentage of 10%) is 1.94. The resultant silica mesoporous microspheres have distinctive pore structures, with a pore volume of more than 1.0 cm3/g, an average pore size of 11.35 nm, and a median pore size of 13.4 nm. The silica mesoporous microspheres with a large particle size, uniform particle size distribution, large average pore size and pore volume, and narrow mesopore size distribution can basically meet the requirements of preparative liquid chromatographic columns.