Morphology controlling of micrometer-sized mesoporous silica spheres assisted by polymers of polyethylene glycol and methyl cellulose

Zhiteng Zhang,Liming Yang,Yujun Wang,Guangsheng Luo,Youyuan Dai
DOI: https://doi.org/10.1016/j.micromeso.2008.02.018
IF: 5.876
2008-01-01
Microporous and Mesoporous Materials
Abstract:Based on the PEG (polyethylene glycol)’s function of bridging flocculation and the MC (methyl cellulose)’s function of formation of liquid crystal in aqueous solution, the morphology of micrometer-sized mesoporous silica spheres with good dispersivity were synthesized by adding the mixture of PEG and MC into the aqueous solution containing F127 and TEOS. It was found that only when PEG was added, the micrometer sized spheres could be synthesized, the spheres possess meso-pores from 2.5nm to 3.0nm, and the specific surface area was from 744m2/g to 861m2/g by changing the amount of PEG, but the dispersibility of microspheres needs to be improved. Only when MC was added, the dispersibility of resultant spheres was good, but the out surface of spheres was not smooth. Then, when suitable amount of PEG and MC were simultaneously added, the spheres with good dispersibility and smooth out surface were obtained.
What problem does this paper attempt to address?