Abstract:Electroplating sludge is extensively produced in chemical precipitation-based treatment of electroplating wastewater. It poses a huge threat to environmental safety if not properly disposed, ascribed to its high contents of heavy metals. An innovative metallurgical approach was proposed a to recycle Cu, Cr, and Ni from it. Ammonia leaching was firstly performed to selectively leach Cu from Cr, in which the Cu oxide and sulfide were leached into the leachate while the Cr oxide and Ni carbide (NiCx) retained in the residue. (NH4)2SO4 increased the Cu leaching rate via increasing the dissolved oxygen amount in the ammonia leachate and converting CuS to Cu2+. Under the optimal conditions, the leaching efficiency of Cu achieved 96.5 % while that of Cr was only 0.1 %. In the followed aluminothermic reduction, C in the leaching residue could be effectively removed via a thermal oxidation, which in turn decreased the formation of a C-containing compound of high melting point and benefited the Cr and Ni recovery. Cr and Ni from the residue were reduced and recovered in a Cr-Ni alloy, and the reductant of Al first changed to a refractory Al2O3 and then transformed to a low melting point 12CaO·7Al2O3 with the additive of CaO. This transformation increased the molten slag fluidity and promoted the separation of Cr-Ni alloy from slag. Moreover, the excessive Al increased the Cr and Ni yields and concentrated all of them to be together. Partial Al was used as reductant, and the other Al transferred into Cr-Ni alloy to decrease its melting point. Cr and Ni contents in the smelting slag could be decreased to 0.11 wt% and 0.12 wt% respectively, showing an efficient recovery. This work provided a high efficiency method to recover Cu, Cr, and Ni from waste electroplating sludge.

Utilization of Nickel Slag Using Selective Reduction Followed by Magnetic Separation

Recovery of valuable metals from electroplating sludge with reducing additives via vitrification

Recovery of Valuable Metals from Nickel Smelting Slag Based on Reduction and Sulfurization Modification

Recovery of Fe, Ni, Co, and Cu from Nickel Converter Slag through Oxidation and Reduction

Comprehensive Recovery of Multisource Metallurgical Wastes: Recycling Nickel Slag by Aluminum Dross with Converter-Slag Addition

Recovery of Cu and Ni in Electroplating Sludge by a Low-Temperature Alkaline Smelting Technique

Extraction of ferronickel concentrate from laterite nickel ore by reduction roasting-magnetic separation using spent cathode carbon

Effect Of Roasting Temperature On Phase Transformation In Co-Reduction Roasting Of Nickel Slag

An approach of cobalt recovery from waste copper converter slags using pig iron as capturing agent and simultaneous recovery of copper and tin

Efficient Utilization of Limonite Nickel Laterite to Prepare Ferronickel by the Selective Reduction Smelting Process

Stepwise Utilization Process to Recover Valuable Components from Copper Slag

Establishment of a Hydrometallurgical Scheme for the Recovery of Copper, Nickel, and Cobalt from Smelter Slag and Its Economic Evaluation

Enrichment Characteristics of Cr in Chromium Slag after Pre-Reduction and Melting/Magnetic Separation Treatment

Recovery of Ni matte from Ni-bearing electroplating sludge

Recovery of valuable metals from copper slag

An efficient approach to utilize copper smelting slag: Separating nonferrous metals and reducing iron oxide at high temperature

Recovery of pure nickel powder from petroleum refinery sludge via a process consisted of leaching, cementation, precipitation, solvent extraction, and chemical reduction

Recovery of nickel and iron from ferronickel powder and high nickel matte via the atmospheric leaching-hematite precipitation process

Increase in Recovery Efficiency of Iron-Containing Components from Ash and Slag Material (Coal Combustion Waste) by Magnetic Separation

Study on Separation of Iron from Waste Slag of Pyrite Processing

A metallurgical approach for separation and recovery of Cu, Cr, and Ni from electroplating sludge