Abstract:Highly ordered hexagonal mesoporous silica materials (JLU-20) with uniform pore sizes have been successfully synthesized at high temperature (150-220degreesC) by using fluorocarbon-hydrocarbon surfactant mixtures. The fluorocarbon-hydrocarbon surfactant mixtures combine the advantages of both stable fluorocarbon surfactants and ordered hydrocarbon surfactants, giving ordered and stable mixed micelles at high temperature (150-220degreesC). Mesoporous JLU-20 shows extraordinary stability towards hydrothermal treatment (100% steam at 800degreesC for 2 h or boiling water for 80 h), thermal treatment (calcination at 1000degreesC for 4 h), and toward mechanical treatment (compressed at 740 MPa). Transmission electron microscopy images of JLU-20 show well-ordered hexagonal arrays of mesopores with one-dimensional (M) channels and further confirm that JLU-20 has a two-dimensional (2D) hexagonal (P6mm) mesostructure. Si-29 HR MAS NMR spectra of as-synthesized JLU-20 shows that JLU-20 is primarily made up of fully condensed Q(4) silica units (delta = - 112 ppm) with a small contribution from incompletely cross-linked Q(3) (delta = - 102 ppm) as deduced from the very high Q(4)/Q(3) ratio of 6.5, indicating that the mesoporous walls of JLU-20 are fully condensed. Such unique structural features should be directly attributed to the high-temperature synthesis, which is responsible for the observed high thermal, hydrothermal, and mechanical stability of the mesoporous silica materials with well-ordered hexagonal symmetry. Furthermore, the concept of "high-temperature-synthesis" is successfully extended to the preparation of three-dimensional (3D) cubic mesoporous silica materials by the assistance of a fluorocarbon surfactant as a co-template. The obtained material, designated JLU-21, has a well-ordered cubic Im3m mesostructure with fully condensed pore walls and shows unusually high hydrothermal stability, as compared with conventional cubic mesoporous silica materials such as SBA-16.

F− assistant synthesis of ultra-hydrothermally stable mesoporous silica by using nonionic organosilicon surfactant as templates

Design and Synthesis of Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at High Temperature from a Mixture of Polymer Surfactant with Small Organic Ammonium.

Hydrothermal Transformation and Characterization of Porous Silica Templated by Surfactants

High-temperature synthesis of stable ordered mesoporous silica materials by using fluorocarbon-hydrocarbon surfactant mixtures.

Semi-fluorinated Surfactant Syntheses of Ordered Porous Materials with Tailorable Pore Sizes

Novel synthesis of high hydrothermal stability and long-range order MCM-48 with a convenient method

Fluoride-Induced Reduction of CTAB Template Amount for the Formation of MCM-48 Mesoporous Molecular Sieve

Influences of anions X-(F-, Cl-, Br-) on synthesis and properties of mesoporous molecular sieve MCM -41

Preparation of Ordered 2-D Hexagonal Mesoporous Silica with Ultra Thick Pore Walls Using a Novel Nonionic Organosilicon Surfactant

Influence of Organic Structure-Directing Agents on Fluoride Dynamics in As-Synthesized Silicalite-1

Ordering improvement of mesoporous silica materials templated from semi-fluorinated nonionic surfactants by introduction of organic additives

Synthesis of silica mesoporous crystals with controlled structure and morphology using gemini surfactant

The Search of Promoters for Silica Condensation and Rational Synthesis of Hydrothermally Stable and Well Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at Conventional Temperature

Stable Ordered Mesoporous Silica Materials Templated by High-Temperature Stable Surfactant Micelle in Alkaline Media

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Quiescent non-ionic surfactant assembly of mesoporous materials under basic conditions

Effect of fluoride ions on the stability of SAPO-11 molecular sieves

Transformation of Lamellar Silicate into the Mesoporous Molecular Sieve MCM-41

High temperature synthesis of hydrothermally stable micro-mesoporous silica and Al-doped mesoporous silica via rigid template

Synthesis of mesostructured silica with strongly hydrophilic surfactant templates

SYNTHESIS OF MESOPOROUS MOLECULAR SIEVES WITH SECONDARY BUILDING UNITS OF β ZEOLITE AT LOW SURFACTANT CONCENTRATION