Abstract:A family of highly ordered mesoporous (20-300 Angstrom) silica structures have been synthesized by the use of commercially available nonionic alkyl poly(ethylene oxide) (PEO) oligomeric surfactants and poly(alkylene oxide) block copolymers in acid media. Periodic arrangements of mescoscopically ordered pores with cubic 1m (3) over bar m, cubic Pm (3) over bar m (or others), 3-d hexagonal (P6(3)/mmc), 2-d hexagonal (p6mm), and lamellar (L-alpha) symmetries have been prepared. Under acidic conditions at room temperature, the nonionic oligomeric surfactants frequently form cubic or 3-d hexagonal mesoporous silica structures, while the nonionic triblock copolymers tend to form hexagonal (p6mm) mesoporous silica structures. A cubic mesoporous silica structure (SBA-11) with Pm (3) over bar m diffraction symmetry has been synthesized in the presence of C16H33(OCH2CH2)(10)OH (C16EO10) surfactant species, while a 3-d hexagonal (P6(3)/mmc) mesoporous silica structure (SBA-12) results when C18EO10 is used. Surfactants with short EO segments tend to form lamellar mesostructured silica at room temperature. Hexagonal mesoporous silica structures with d(100) spacings of 64-77 Angstrom can be synthesized at 100 degrees C by using oligomeric nonionic surfactants. Highly ordered hexagonal mesoporous silica structures (SBA-15) with unusually large d(100) spacings of 104-320 A have been synthesized in the presence of triblock poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide) (PEO-PPO-PEO) copolymers. SBA-15 mesoporous structures have been prepared with BET surface areas of 690-1040 m(2)/g, pore sizes of 46-300 Angstrom, silica wall thicknesses of 31-64 Angstrom, and pore volumes as large as 2.5 cm(3)/g. A novel cubic (Im (3) over bar m) cage-structured mesoporous silica structure (SBA-16) with a large cell parameter (a = 176 ii) has been synthesized using triblock copolymers with large PEO segments. The EO/PO ratio of the copolymers can be used to control the formation of the silica mesophase: lowering this ratio of the triblock copolymer moieties promotes the formation of lamellar mesostructured silica, while higher ratios favor cubic mesostructured silica. Cubic mesoporous structures are also obtained when star diblock copolymers are used as structure-directing agents. The calcined ordered mesoporous silicas reported in this paper an thermally stable in boiling water for at least 48 h. The assembly of the inorganic and organic periodic composite materials appears to lake place by a hydrogen bonding (S-0 H+)(X-I+) pathway. The assembly race r increases with increasing concentration of [H+] and [Cl-], according to the kinetic expression r = k[H+](0.31)[Cl-](0.31).

Quiescent non-ionic surfactant assembly of mesoporous materials under basic conditions

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

Nonionic Triblock and Star Diblock Copolymer and Oligomeric Surfactant Syntheses of Highly Ordered, Hydrothermally Stable, Mesoporous Silica Structures

Syntheses of High-Quality Mesoporous Materials Directed by Blends of Nonionic Amphiphiles under Nonaqueous Conditions

Mesoporous Structure Control of Silica in Room-Temperature Synthesis under Basic Conditions

Synthesis of Microporous Silica in the Presence of Dodecyldimethylbenzylammonium Chloride Surfactant

Synthesis of ordered small pore mesoporous silicates with tailorable pore structures and sizes by polyoxyethylene alkyl amine surfactant

Anionic Surfactant Induced Mesophase Transformation to Synthesize Highly Ordered Large-Pore Mesoporous Silica Structures

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Synthesis of Mesoporous Silica from Commercial Poly(ethylene Oxide)/poly(butylene Oxide) Copolymers: Toward the Rational Design of Ordered Mesoporous Materials

Synthesis of mesostructured silica with strongly hydrophilic surfactant templates

A Facile Preparation of Transparent and Monolithic Mesoporous Silica Materials

Design and Synthesis of Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at High Temperature from a Mixture of Polymer Surfactant with Small Organic Ammonium.

Synthesis of mesoporous silica with ionic liquid surfactant as template

Mesoporous silicas of hierarchical structure by hydrothermal surfactant-templating under mild alkali conditions

Design and Synthesis of Microporous and Micro/Mesoporous Silica Materials with Excellent Adsorption Properties Via Self-Assembly of Silica Species with Tetraethyl Ammonium in Acidic Aqueous Media

Synthesis of Mesoporous Molecular Sieves with Secondary Building Units of Y Zeolite by Using Surfactants in Low Concentration as Template

Generalized Syntheses of Large-Pore Mesoporous Metal Oxides with Semicrystalline Frameworks

Formation of Monodisperse Mesoporous Silica Microparticles Via Spray-Drying

Continuous Formation of Supported Unusual Mesostructured Silica Films by Sol−Gel Dip Coating