Abstract:Several interactions can occur between the liquid clad and solid core alloys during brazing of multi-layered Al brazing sheets used in automotive heat exchanger fabrication. The objective of the current study is to evaluate the use of a physical barrier layer between the clad and core alloys to prevent the occurrence of certain solid–liquid interactions during brazing. A novel brazing sheet comprised an AA4045 clad, AA1100 barrier layer, and Al–1.95 Mg–1.5Mn–0.5Cu core alloy (NS) was investigated and compared with a commercially available AA4045/X901 brazing sheet (CS). Interrupted tensile tests were performed to impart strains between 0 and 10% in both sheet conditions prior to brazing. Differential scanning calorimetry (DSC) was used to measure the brazing characteristics through the ratio of solidification peak energy to initial melting peak energy after a 3-min hold at 600 °C (i.e., ΔHsol/ΔHmelt). The post-braze microstructures of DSC samples and samples subjected to furnace brazing were investigated. The ΔHsol/ΔHmelt ratio for both CS and NS conditions exhibited a non-linear relationship with the level of applied strain prior to brazing, but the nature of the relationship was different for the two sheets. Liquid film migration (LFM) was generally observed in CS conditions exhibiting low values of ΔHsol/ΔHmelt. The NS barrier layer was found to effectively prevent LFM in strained brazing sheet, but diffusional solidification of the clad layer still resulted in relatively low ΔHsol/ΔHmelt values at low levels of pre-strain. It was also found that the post-braze microstructures of samples heat treated in the DSC and furnace were different, with furnace-treated samples containing a greater volume of Al–Si eutectic due to the shorter time at elevated temperatures. It is concluded that the barrier layer can be an effective method to prevent liquid film migration in strained brazing sheet.

Formation of Microlayers of Clad Residue on Aluminium Brazing Sheet During Melting and Resolidification in Brazing Process

Diffusion-Controlled Melting and Re-Solidification of Metal Micro Layers on A Reactive Substrate

Non-Equilibrium Diffusion-Controlled Melting and Re-Solidification of Thin Metal Layers on a Reactive Substrate

Molten aluminum equilibrium membrane formed during controlled atmosphere brazing

Microstructure and Mechanical Properties of 4343/3003/6111/3003 Four-Layer Al Clad Sheets Subjected to Different Conditions

Diffusion behavior of silicon at interface of Al clad sheet and joint formation

Residual clad formation and aluminum brazed joint topology prediction

Effect of pre-strain on the brazing characteristics of a high-strength aluminum brazing sheet with a barrier layer

Metallurgical interactions in solid/liquid diffusion couples of AA4343/AA3xxx/AA4343 layered aluminum sheet

Microstructure and Copper Contamination Phenomenon of Laser Cladded Aluminum Bronze Coatings on Carbon Steel Surface

Interfacial Microstructure and Forming Mechanism of Brazing Cf/Al Composite with Al–Si Filler

An Analysis of an Impact of the Background Atmosphere on the Aluminum Brazing Joint Formation

Effect of Processing Parameters on Microstructure in Brazing of Al–Si Alloys

Understanding the Effect of Holding Time on Interfacial Microstructure Evolution and Mechanical Properties of Ti3AlC2/Zr-4 Brazed Joints

Solid state Si diffusion and joint formation involving aluminum brazing sheet

Solidification Behaviour and the Evolution of Microstructure in the Laser Cladding of Aluminium on Magnesium Substrate

Brazing of Transparent Polycrystalline Al2O3 and GH99 with the Assistance of (cu, Ni) Solid Solution Cladding Layer

Capillary Filling Process During Ultrasonically Brazing of Aluminium Matrix Composites

Formation of Liquid Pools Entrapped Within Solid Grains of Za27 Alloys During Partial Remelting

Scaling of Molten Metal Brazing Phenomena: Prolegomena for Model Formulation